研究了碳化混凝土再碱化过程中钢筋在Ca(OH)2溶液中的电极表面电化学反应,采用电化学测量技术结合模拟试验考察了电极表面发生各类反应的可能性.结果表明:再碱化过程中,钢筋电极表面的电化学反应与钢筋表面的状态有密切关系,当电极表面存在锈蚀层时,再碱化过程析氢反应和氧化铁的还原同时发生,并使表面氧化层的价态逐渐降低,在电极表面形成金属铁,析氢过程产生的OH-使钢筋周围混凝土的碱性提高.
参考文献
| [1] | 李建勇,杨红玲.国外混凝土钢筋锈蚀破坏的修复和保护技术[J].建筑技术,2002(07):491-493. |
| [2] | Lorenzo Fedrizzi;Francesca Azzolini;Pier Luigi Bonora .The use of migrating corrosion inhibitors to repair motorways' concrete structures contaminated by chlorides[J].Cement and Concrete Research,2005(3):551-561. |
| [3] | M. Siegwart;J.F. Lyness;B.J. McFarland .The effect of electrochemical chloride extraction on pre-stressed concrete[J].Construction and Building Materials,2005(8):585-594. |
| [4] | K. Kawamata .Electrochemical Corrosion Control Method for Concrete Structure[J].Corrosion Engineering,2004(9):469-479. |
| [5] | C. Andrade;M. Castellote;J. Sarria .Evolution of pore solution chemistry, electro-osmosis and rebar corrosion rate induced by realkalisation[J].Materials and structures,1999(220):427-436. |
| [6] | 朱雅仙.碳化混凝土再碱化技术的研究[J].水运工程,2001(06):12-14,16. |
| [7] | 刘可高,朱慧.火灾损伤钢筋混凝土电化学再碱化技术的研究[J].建筑技术开发,2004(12):44-47. |
| [8] | 屈文俊,陈璐,刘于飞.碳化混凝土结构的再碱化维修技术[J].建筑结构,2001(09):58-60. |
| [9] | 朱鹏,屈文俊.碳化混凝土再碱化控制理论研究的探讨[J].材料导报,2006(03):101-103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%