采用化学沉淀的方法,在氧化锆粉体表面包覆了10~20 nm厚的铝和钴的氢氧化物,高温烧结后制备了CoAl2O4/ZrO2复相陶瓷.由于高温下COO的挥发,少量过剩的Al2O3扩散进入CoAl2o4晶格而导致其晶格常数变小.XRD相分析发现CoO和Alzo3的引入对基体氧化锆的四方相含量没有显著影响.研究结果表明,化学沉淀包覆的方法有利于反应物的均匀混合,缩短传质距离而促进固相反应,并在一定程度上保证复相陶瓷结构的均匀性.
参考文献
[1] | Ciacchi F T;Crane K M;Badwal SPS .[J].Solid State Ionicis,1994,73:49. |
[2] | Wen TL.;Wang D.;Chen M.;Tu H.;Lu Z.;Zhang Z.;Nie H.;Huang W. .Material research for planar SOFC stack[J].Solid state ionics,2002(3/4):513-519. |
[3] | Luo J.;Almond P. .Ionic mobilities and association energies from an analysis of electrical impedance of ZrO_2-Y_2O_3 alloys[J].Journal of the American Ceramic Society,2000(7):1703-1708. |
[4] | Yu S B;Wu Q H;Tabib-Azar M et al.[J].Sensors and Actuators B:Chemical,2002,85(03):212. |
[5] | Panpranot J;Taochaiyaphum N;Praserthdam P .[J].Materials Chemistry and Physics,2005,94(2-3):207. |
[6] | Xiong HF;Zhang YH;Liew K;Li JL .Catalytic performance of zirconium-modified Co/Al2O3 for Fischer-Tropsch synthesis[J].Journal of molecular catalysis, A. Chemical,2005(1/2):145-151. |
[7] | Bondioli F.;Leonelli C.;Manfredini T.;Ferrari AM. .Syntheses of Fe2O3/silica red inorganic inclusion pigments for ceramic applications[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,1998(5):723-729. |
[8] | Bolt P H;Habraken FHPM;Geus J W .[J].Journal of Solid State Chemistry,1998,135(01):59. |
[9] | Otero Arean C;Mentruit Penarroya M et al.[J].Materials Letters,1999,39:22. |
[10] | 牟军;郦剑;郭绍义 .[J].材料科学与工程,1994,12(03):6. |
[11] | Levin E M.Phase Diagrams for Ceramists[M].Ohio:American Ceramics Society,1975 |
[12] | Chiou Y H;Lin S T .[J].Ceramics International,1996,22:249. |
[13] | Vladimir V S;Markus w;Horst H .[J].Journal of the American Ceramic Society,2000,83(08):1853. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%