在连铸连轧生产线采用铁素体轧制技术制备了低碳钢热轧薄板,并对所制备的薄板进行了力学性能、组织及织构分析.结果表明,铁索体轧制低碳钢薄板的组织为完全再结晶铁素体和少量珠光体,平均晶粒尺寸30μm左右.相对于常规奥氏体轧制,铁素体轧制薄板的屈服强度下降了20%左右,伸长率及应变硬化指数与之相当.横向、纵向及45°方向的塑性应变比值分别为0.76、0.35、0.70,明显低于常规奥氏体轧制.低碳钢的动态应变时效行为是导致其铁素体轧制薄板塑性应变比值较低的主要原因.
参考文献
| [1] | Barnett M R;Jonas J J .Influence of Ferrite Rolling Temperature on Microstructure and Ttexture in Deformed Low C and IF Steels[J].ISIJ International,1997,37(07):697. |
| [2] | Matsuoka Saiji;Sakata Kei;Satoh Susumu et al.Effect of Hot-Rolling Strain Rate in the Ferrite Region on the Recrystallization Texture of Extra-Low C Steel Sheets[J].ISIJ International,1994,34(01):77. |
| [3] | 赵鸿金;朱伏先;王国栋 等.终轧及卷取温度对热轧SP325钢板织构与深冲性能的影响[J].东北大学学报(自然科学版),1994,5(04):374. |
| [4] | 钱匡武,彭开萍,陈文哲.金属动态应变时效现象中的"锯齿屈服"[J].福建工程学院学报,2003(01):4-8. |
| [5] | Hashimoto Shunichi;Tsukatani Ichiro;Kashima Takahiro et al.Development of Hot-Rolled Steel Sheet With a High R-Value by Rolling in Ferrite Region With Lubrication[J].R & D:Research and Development Kobe Steel Engineering Reports,1998,48(01):14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%