采用晶体取向分布函数方法(ODF)和X射线衍射测定板面晶面衍射强度研究和分析了在高纯铝中加入微量稀土(Y)对箔材织构演变的影响.研究结果表明:添加微量稀土,能改变高纯铝箔中变形织构组分的相对强度,随稀土含量增加,黄铜取向密度增加,S织构组分减少,成品退火箔材中立方织构含量随稀土含量增加就相应减少.当稀土含量为0.0030%时,成品退火箔材中立方织构取向密度最大.其作用机理是稀土元素Y化学活性强,能与铁等微量杂质元素形成一系列化合物.析出后可净化基体,降低基体中铁等杂质的浓度,消除杂质元素对高纯铝箔中立方织构形成的不利影响.
参考文献
| [1] | Vante H E;Furu T;Nes E .[J].材料科学与工艺(英文版),1995,12:201. |
| [2] | HjelenJ;φrsund R;Nes E .[J].Acta Materialia,1991(39):1377. |
| [3] | Engler O .A[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1999,30:1517. |
| [4] | Dillamore I L;Katoh H .Science[J].Metal Science Journal,1974,8:73. |
| [5] | Dons A L;Nes E .[J].材料科学与工艺(英文版),1986,2:8. |
| [6] | Engler O;Moo-Young H .Engineering[J].Materials Science and Engineering,1999,A271:371. |
| [7] | Suzuki T;Arai K;Shiga M et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16A:27. |
| [8] | ItoK;MusickR;LuckeK .[J].Acta Metallurgy,1983,31(12):2137. |
| [9] | Ito K;LiuckeK;RixenR .[J].Zeitschrift fur Metallkunde,1976,67(05):338. |
| [10] | Hug I H;Bichsel H.[J].Metal Treatment and Drop Forging,1862:258. |
| [11] | Bunge H J.Mathematischa Methoden der Textur Analyse[C].Akademie Verlag,Berlin,1969 |
| [12] | 孙伟成;张淑荣;侯爱芹.稀土在铝合金中的行为[M].北京:兵器工业出版社,1992 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%