采用高温固相法制备Y3-xAl5O12:xCe3+(x=0.05～0.9)荧光粉,利用荧光光谱仪、X射线衍射仪和扫描电镜等对样品的发光性能、物相和形貌进行了测试分析.研究了Ce3+浓度、助熔剂、灼烧温度、灼烧时间等对样品发光性能的影响.结果表明,以Al(OH)3为原料,采用氟化物助熔剂可以获得颗粒细小均匀的荧光粉,研究结果对荧光粉的生产具有一定的意义.
参考文献
| [1] | Narukawa Y;Niki I;Izuno K et al.Phosphor-conversion white light emitting diode using InGaN near-ultraviolet chip[J].Applied Physics,2002,41(04):L371-L373. |
| [2] | 徐时清,金尚忠,王宝玲,张丽艳,赵士龙,李晨霞.固体照明光源-白光LED的研究进展[J].中国计量学院学报,2006(03):188-191. |
| [3] | 罗昔贤,曹望和,孙菲.硅酸盐基质白光LED用宽激发带发光材料研究进展[J].科学通报,2008(09):1010-1016. |
| [4] | Kong Li,Gan Shucai,Hong Guangyan,Zhang Jilin.Relationship between Crystal Structure and Luminescence Properties of (Y0.96-xLnxCe0.04)3Al5O12 (Ln=Gd, La, Lu) Phosphors[J].稀土学报（英文版）,2007(06):692-696. |
| [5] | Yang R;Qin J;Li M et al.Synthesis of yttrium aluminium garnet(YAG) powder by homogeneous precipitation combined with supercritical carbon dioxide or ethanol fluid drying[J].Journal of the Ceramic Society,2008,28(15):2903-2914. |
| [6] | 孙海鹰,张希艳,王能利,米晓云,刘全生.YAG∶ Ce荧光粉的柠檬酸-凝胶法合成与表征[J].硅酸盐通报,2009(06):1259-1262. |
| [7] | 孙海鹰,张希艳,王能利,米晓云,刘全生.丙二酸溶胶-凝胶法合成亚微米级YAG：Ce,Gd黄色荧光粉[J].硅酸盐通报,2010(01):94-97,106. |
| [8] | 刘全生,章瑞铄,方潇功,黄原亮,张希艳,孟繁艳,董飞,孟庆贺.稀土掺杂Sr3Al2O6红色发光材料的制备与表征[J].硅酸盐通报,2010(03):530-533. |
| [9] | 王飞,田一光,张乔,赵文光.SrAl2Si2O8：Eu2+蓝色荧光粉制备条件优化及助熔剂作用研究[J].硅酸盐通报,2011(02):457-461. |
| [10] | Michael K. Cinibulk .Synthesis of yttrium aluminum garnet from a mixed-metal citrate precursor[J].Journal of the American Ceramic Society,2000(5):1276-1278. |
| [11] | Pan, YX;Wu, MM;Su, Q .Tailored photoluminescence of YAG : Ce phosphor through various methods[J].The journal of physics and chemistry of solids,2004(5):845-850. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%