The Ce-Zr-La-O solid solution was prepared by the sol-gel method. The structure and the redox behavior of Ce-Zr-La-O solid solution and CuO/Ce-Zr-La-O catalysts were investigated by using XRD, Raman and TPR techniques. The result shows that the reduction capability of Ce0.7Zr0.3-yLayO solid solution is related to content of La. Appropriate content of La can enhance the redox capability of the solid solution. The oxidation activity of the CuO(6%)/Ce0.7Zr0.15La0.15O catalyst is the highest. CuO, which finely dispersed and interacted with the support, is the site of oxidation activity.
参考文献
| [1] | Trovarelli A .Catalytic properties of ceria and CeO2-containing materials[J].Catalysis Review-Science and Engineering,1996,38:439. |
| [2] | Trovarelli A.;Llorca J.;Deleitenburg C.;Dolcetti G.;Kiss JT.;Zamar F. .NANOPHASE FLUORITE-STRUCTURED CEO2-ZRO2 CATALYSTS PREPARED BY HIGH-ENERGY MECHANICAL MILLING - ANALYSIS OF LOW-TEMPERATURE REDOX ACTIVITY AND OXYGEN STORAGE CAPACITY[J].Journal of Catalysis,1997(2):490-502. |
| [3] | Formasiero P;Monte R D;Rao G et al.Rh-loaded CeO2-ZrO2 solid solution as highly efficient oxygen exchanges: dependence of the reduction behavior and the oxygen storage capacity on the structural properties[J].Journal of Catalysis,1995,151:168. |
| [4] | Formasiero P;Kaspar J;Graziani M .Redox behavior of high surface area Rh-loaded Ce0.5Zr0.5O2 mixed oxide[J].Journal of Catalysis,1997,167:576. |
| [5] | 罗孟飞,林瑞,陈敏,袁贤鑫,郑小明.Ce-Zr-O固溶体的制备和表征[J].中国稀土学报,2000(01):35-37. |
| [6] | Luo MF.;Zheng XM.;Zhong YJ.;Wu TH.;Lu GL. .Redox properties of CexZr1-xO2 mixed oxides prepared by the sol-gel method[J].Journal of Materials Science Letters,1998(18):1553-1557. |
| [7] | Luo M F;Zheng X M .Redox behavior and catalytic properties of Ce0.5Zr0.5O2-supported palladium catalysts[J].Applied Catalysis,1999,189:15. |
| [8] | Wang X Y;Wan Y;Lu G Z .Effect of lanthanum on methanol fuel exhoust deep oxidation over palladium catlayst[J].Journal of Rare Earths,2003,21(01):51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%