采用机械合金化法制粉、液相烧结和致密化处理工艺,制备了低质量分数的Mo-Cu合金.通过X射线衍射和扫描电镜对Mo-Cu复合粉末形貌、液相烧结和变形加工后合金显微组织进行了分析,研究了各种工艺参数对Mo-Cu合金致密性、拉伸强度和延伸率的影响.结果表明,采用高能球磨机械合金化和液相烧结,可获得相对密度高达98.2%的Mo-Cu合金, 再经致密化变形加工处理后,可获得全致密的Mo-Cu合金,在40%变形率的条件下,拉伸强度可达到569MPa,延伸率为6.3%.
参考文献
| [1] | Suryanarayana C .[J].Materials Science,2001,46:181-184. |
| [2] | Suryanarayana C et al.[J].Materials Today,2005,11:62. |
| [3] | 刘海彦,李增峰,汤慧萍,高广瑞,黄原平.机械合金化制备钼铜复合材料[J].功能材料,2004(z1):3294-3296. |
| [4] | Alam S N .[J].Materials Science and Engineering,2006,433:161-168. |
| [5] | Maneshian M H;Simchi A .[J].Journal of Alloys and Compounds,2008,463:153-159. |
| [6] | Ivanov E Y;Suryanarayana C;Bryskin B D .[J].Materials Science and Engineering,1998,251:255-261. |
| [7] | Martinez V;Aguilar C;Marin J et al.[J].Materials Letters,2007,61:929-933. |
| [8] | Aguilar C;Marin J;Ordonez S et al.[J].Materials Science and Engineering,2007,464:288-294. |
| [9] | John L. Johnson;Randall M. German .Powder metallurgy processing of Mo-Cu for thermal management applications[J].International Journal of Powder Metallurgy,1999(8):39-48. |
| [10] | 南海,曲选辉,方玉诚,何新波.电子封装用注射成形Mo/Cu合金烧结工艺的研究[J].粉末冶金工业,2004(06):1-5. |
| [11] | 张朝晖,王富耻,李树奎.静液挤压钨合金的显微组织与力学性能[J].中国有色金属学报,2001(z1):88-91. |
| [12] | 张朝晖,王富耻,李树奎.钨合金的静液挤压变形强化[J].兵工学报,2002(02):224-227. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%