Alloys of Mg-Zn-La system in Mg rich corner at 350℃ have been prepared in this study. Scanning electron microscopy (SEM), electron probe microanalysis with energy dispersive X-ray spectroscopy (EPMA-EDS), and X-ray diffraction (XRD) have been used to identify the phase equilibrium and the composition of each phase in the alloys. As a result, the isothermal section of Mg-Zn-La system in Mg rich corner at 350℃ has been determined. The result shows that, in addition to some binary phases, there exists a linear ternary compound called T-phase in Mg-Zn-La system at 350℃, in which the La content is about 8 at. pct±0.4 at. pct and the Zn content is 8 at. pct-48 at. pct. The T-phase has a C-centered orthorhombic crystal structure, and the lattice parameters are a=0.965-1.020 nm, b=1.121-1.142 nm, c=0.950-0.977 nm.
参考文献
[1] | T V Dobatkina;E V Muratova;E I Drozdova .[J].Russian Metallurgy,1987,1:205. |
[2] | P Villars;A Prince;H Okamoto.Handbook of Ternary Alloy Phase Diagrams[M].CD-ROM,ASM International,USA,1997 |
[3] | A A Nayeb-Hashemi;J B Clark.Phase Diagrams of Binary Magnesium Alloy ASM[M].Metals Park,OH,USA,1996 |
[4] | M. GIOVANNINI;A. SACCONE;R. MARAZZA;R. FERRO .The Isothermal Section at 500℃ of the Y-La-Mg Ternary System[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1995(1):5-10. |
[5] | C P Guo;Z M Du .[J].Journal of Alloys and Compounds,2004,385:109. |
[6] | L Rolla;A IandeUi .[J].Ricerca Scientifica,1941,20:1216. |
[7] | J B Clark;L Zabdyr;Z Moser.Phase Diagrams of Binary Magnesium Alloys[M].ASM International,Metals Park,OH,USA,1988 |
[8] | R Agarwal;S G Fries;H L Lukas;G Petzow G Petzow,F Sommer,T G Chart and G Effenberg .[J].Z MetaUkd,1992,839:216. |
[9] | T B Massalski;H Okamoto;P R Subramanian;L Kacprzak.Binary Alloy Phase Diagrams[M].CD-ROM,ASM International,USA,1996 |
[10] | L Y Wei .[J].Journal of Materials Science,1997,32:3335. |
[11] | C J Rossouw;C J Bettles;T J Davis;C T Forwood,P R Miller and K Venkatesan .[J].Acta Crystallographica,2001,51A:321. |
[12] | L Y Wei;G L Dunlop;H Westengen .[J].Metallurgical and Materials Transactions,1994,26A:1947. |
[13] | J B Clark;F N Rhines .[J].Journal of Metals,1957,209:425. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%