以碱矿渣水泥为胶凝材料、采用压缩空气发泡方式制备出一种新型泡沫混凝土,并对该泡沫混凝土基本性能进行了研究.结果表明:当密度在250 ～ 600 kg/m3,碱矿渣水泥泡沫混凝土导热系数在0.070 ～0.139 W/(m·K),龄期为28 d时抗压强度在0.6～3.5 MPa.与普通水泥制备的泡沫混凝土相比,碱矿渣泡沫混凝土具有导热系数相近、抗压强度更高的特点.
参考文献
| [1] | 吴兆春.泡沫混凝土--未来建筑节能重要的保温材料发展方向[J].砖瓦,2012(1):58-60. |
| [2] | 吕红魁.泡沫混凝土的应用及施工质量控制要点[J].四川建材,2012(01):91-92. |
| [3] | 张英;杨小芳;赵芊;于水军.泡沫混凝土在屋面保温工程中的应用[J].新型建筑材料,2011(9):19-21. |
| [4] | 黄政宇;孙庆丰;周志敏.硅酸盐-硫铝酸盐水泥超轻泡沫混凝土孔结构及性能研究[J].硅酸盐通报,2013(9):1894-1899. |
| [5] | Yue, Li;Bing, Chen.New Type of Super-Lightweight Magnesium Phosphate Cement Foamed Concrete[J].Journal of Materials in Civil Engineering,20151(1) |
| [6] | E. Prud'homme;P. Michaud;E. Joussein.Silica fume as porogent agent in geo-materials at low temperature[J].Journal of the European Ceramic Society,20107(7):1641-1648. |
| [7] | F. Gouny;F. Fouchal;P. Maillard;S. Rossignol.A geopolymer mortar for wood and earth structures[J].Construction and Building Materials,2012:188-195. |
| [8] | 吴中伟.绿色高性能混凝土与科技创新[J].建筑材料学报,1998(01):1. |
| [9] | 张雄;黄廷皓;张永娟;高辉;姜曼.Image-Pro Plus混凝土孔结构图像分析方法[J].建筑材料学报,2015(1):177-182. |
| [10] | 何娟;杨长辉.水玻璃激发碱-矿渣水泥的水化放热和凝结性能[J].土木建筑与环境工程,2011(3):147-152. |
| [11] | 何娟;杨长辉;康苏芳.碱-矿渣水泥缓凝问题的研究进展[J].硅酸盐通报,2010(5):1093-1097. |
| [12] | 赵爽 .碱矿渣水泥化特性研究[D].重庆大学,2012. |
| [13] | Vladimir Zivica.Effects of type and dosage of alkaline activator and temperature on the properties of alkali-activated slag mixtures[J].Construction and Building Materials,20077(7):1463-1469. |
| [14] | F.Collins;J.G.Sanjayan.Strength and shrinkage properties of alkali-activated slag concrete placed into a large column[J].Cement and Concrete Research,19995(5):659-666. |
| [15] | Alessandra Mendes;Jay G. Sanjayan;Frank Collins.Long-term Progressive Deterioration Following Fire Exposure Of Opc Versus Slag Blended Cement Pastes[J].Materials and structures,20091(1):95-101. |
| [16] | Antonio A. Melo Neto;Maria Alba Cincotto;Wellington Repette.Drying and autogenous shrinkage of pastes and mortars with activated slag cement[J].Cement and Concrete Research,20084(4):565-574. |
| [17] | Antonio A. Melo Neto;Maria Alba Cincotto;Wellington Repette.Mechanical properties, drying and autogenous shrinkage of blast furnace slag activated with hydrated lime and gypsum[J].Cement & concrete composites,20104(4):312-318. |
| [18] | 陈科;杨长辉;潘群;赵爽;于泽东.碱-矿渣水泥砂浆的干缩特性[J].重庆大学学报：自然科学版,2012(5):64-68. |
| [19] | 朱明;王方刚;张旭龙;王发洲.泡沫混凝土孔结构与导热性能的关系研究[J].武汉理工大学学报,2013(3):20-25. |
| [20] | 李翔宇;赵霄龙;郭向勇;曹力强.泡沫混凝土导热系数模型及参数修正[J].材料导报,2011(20):146-148,152. |
| [21] | 马保国;赵志广;蹇守卫;苏雷;刘敏.泡沫混凝土干密度试验研究[J].混凝土,2012(6):1-3,6. |
| [22] | Bing Chen;Ning Liu.A novel lightweight concrete-fabrication and its thermal and mechanical properties[J].Construction and Building Materials,2013Jul.(Jul.):691-698. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%