经过多火次锻造得到具有均匀细小等轴组织的TA5钛合金棒材，在600～800℃范围内对其进行不同温度和不同保温时间的退火热处理，研究不同热处理工艺对其显微组织与力学性能的影响。结果表明，热处理温度在700～750℃，保温时间在60～90 min之间时，得到的组织为更加均匀的等轴组织；棒材的抗拉强度为740 MPa左右，屈服强度在595 MPa左右，延伸率在14％左右，强度和塑性达到较好的匹配。
The effects of different heat treatment processes on the microstructure and mechanical properties of TA 5 ti-tanium alloy bars were studied .And the tested TA5 alloy bars had uniform equiaxed microstructure after the process of repeated firing forging .The temperature range of heat treatments were from 600℃to 800℃.The results show that the microstructure of TA5 alloy bars will be more uniform when the heat treatment temperature from 700 ℃to 750 ℃and the holding time from 60 min to 90 min.Under such process condition , the tensile strength is about 740 MPa, the yield strength is about 595 MPa, elongation is about 14%.The strength and plasticity can reach a good match .
参考文献
| [1] | 何书林,冯永琦,王永强,张鹏,徐祝萍.TA5钛合金组织对锻件性能的影响[J].金属学报,2002(z1):204-205. |
| [2] | 稀有金属材料加工手册编写组.稀有金属材料加工手册[M].北京:冶金工业出版社,1984:471-479. |
| [3] | 孙建科,孟祥军,陈春和,刘茵琪.我国船用钛合金研究、应用及发展[J].金属学报,2002(z1):33-36. |
| [4] | 刘兴合 .TA5 钛合金切削特性分析[J].舰船光学,2004,40(03):46-48. |
| [5] | 闵新华,朱益藩,罗月新.变形量对Ti-6Al-2Zr-1Mo-1V合金组织和性能的影响[J].金属学报,2002(z1):181-182. |
| [6] | 张宝昌.有色金属及其热处理[M].西安:西北工业大学出版社,1993:46. |
| [7] | 李东,邓炬,于振涛,吴伟璐.热处理工艺对TA17合金棒材组织的影响[J].热加工工艺,2008(06):59-61. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%