采用拟反应注射成型(RIM)工艺,在经典开环易位催化体系下,将溶有乙烯-醋酸乙烯酯共聚物(EVA)的双环戊二烯(DCPD)进行原位聚合共混,制备了PDCPD/EVA复合材料,从而对PDCPD进行增韧.考察了EVA的相对分子质量及添加量对DCPD聚合反应和复合材料力学性能的影响,运用扫描电镜、差示扫描量热分析、热重分析等对聚合物进行了表征,研究了复合材料的微观形貌、力学性能以及热性能.结果表明,EVA与PDCPD能形成半互穿网络结构,EVA的引入显著提高了材料的冲击性能,其中,EVA用量为5％时冲击性达到最高,可提高85％,拉伸和弯曲强度略有下降,同时材料的热稳定性也有所提高,热分解温度提高了4.2℃,PDCPD/EVA的冲断面呈现韧性断裂.
参考文献
| [1] | Yao, Z.;Zhou, L.-W.;Dai, B.-B.;Cao, K. .Ring-opening metathesis copolymerization of dicyclopentadiene and cyclopentene through reaction injection molding process[J].Journal of Applied Polymer Science,2012(4):2489-2493. |
| [2] | Fengge Gao;Gunter Beyer;Qingchun Yuan .A mechanistic study of fire retardancy of carbon nanotube/ ethylene vinyl acetate copolymers and their clay composites[J].Polymer Degradation and Stability,2005(3):559-564. |
| [3] | Richard J.Pazur;L.Ferrari;H.Meisenheimer .EVM copolymers:The forgotten rubber[J].Rubber World: The Technical Service Magazine for The Rubber Industry,2005(5):27-34. |
| [4] | 付学俊,刘涛,张盈盈,王国成,蒋涛.EVA增韧聚乳酸的性能研究[J].塑料科技,2007(07):50-54. |
| [5] | Yang YS.;Mortaigne B.;Lafontaine E. .CURING STUDY OF DICYCLOPENTADIENE RESIN AND EFFECT OF ELASTOMER ON ITS POLYMER NETWORK[J].Polymer: The International Journal for the Science and Technology of Polymers,1997(5):1121-1130. |
| [6] | 夏敏,罗运军,王兴元.超支化聚合物/环氧树脂体系的固化行为及性能[J].高分子材料科学与工程,2008(02):99-102,106. |
| [7] | 黎华明,刘朋生,陈红飙.聚双环戊二烯的性能研究[J].高分子材料科学与工程,1999(03):169-171. |
| [8] | 陆昶,刘继纯,刘宪俊,张玉清.SBA-15/PDCPD复合材料的阻燃性能[J].复合材料学报,2011(03):35-41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%