主要介绍了高压输气管线延性断裂的特征、形成机制,以及我国在高强高韧性管线钢焊接材料、工艺及焊接性方面的一些研究工作.
参考文献
| [1] | Brian N leis.Characterizing dynamic crack-resistance of pipelines using laboratory-scale practices,Seminar on ductile fracture·prevention in high pressure gas transmission pipeline[J].Langfang China,2000 |
| [2] | Gery M Wilkowski.Ductile fracture arrest methodology for current and future grades of linepipe steels[M].Seminar on ductile fracture·prevention in high pressure gas transmission pipeline Langfang China,2000 |
| [3] | Hiroki Makino.Predication for crack propagation and arrest of shear fracture in ultra-high pressure natural gas pipelines[M].Seminar on ductile fracture·prevention in high pressure gas transmission pipeline Langfang China,2000 |
| [4] | 薛小怀 .X80管线钢埋弧焊用焊丝、工艺及焊接性的研究[D].中国科学院金属研究所,2001. |
| [5] | 钱百年,国旭明,李晶丽,薛小怀.高强度管线钢 X80 的焊接研究[J].焊接,2002(08):14-17. |
| [6] | 国旭明,钱百年,薛小怀,李晶丽,张艳.电磁搅拌对管线钢埋弧焊熔敷金属低温韧性的影响[J].金属学报,2000(02):177-180. |
| [7] | 薛小怀,国旭明,钱百年,楼松年.氩弧重熔对管线钢接头表层组织的影响[J].热加工工艺,2002(04):25-26. |
| [8] | 薛小怀,国旭明,李东,陈怀宁,钱百年,楼松年.外场处理对低合金钢焊接接头组织和性能的影响[J].材料热处理学报,2002(03):10-14. |
| [9] | 薛小怀,钱百年,国旭明,楼松年.氩气保护对埋弧焊焊缝氧氮含量和冲击韧性的影响[J].机械工程材料,2003(03):27-29. |
| [10] | 薛小怀,钱百年,国旭明,楼松年.高强高韧性管线钢埋弧用焊丝的研制[J].焊接学报,2002(05):23-27. |
| [11] | 国旭明 .输气管线用埋弧焊丝的研制及外场处理对熔敷金属显微组织和性能的影响[D].中国科学院金属研究所,2000. |
| [12] | 薛小怀,钱百年,国旭明,于少飞.超低碳贝氏体（ULCB）焊接材料的研究进展[J].焊接学报,2001(04):93-96. |