以丙烯酸丁酯(BA)、甲基丙烯酸甲酯(MMA)、丙烯酸(AA)和丙烯酸羟丙酯(HPA)为主要单体,甲基丙烯酸缩水甘油酯(GMA)做交联固化剂,用半连续乳液合成法制备自交联反应型丙烯酸酯胶粘剂乳液,并将其应用于聚氯乙烯(PVC)与织物的粘结.通过热失重分析法对改性前后胶膜热稳定性进行了分析,研究了丙烯酸(AA)含量对胶粘剂乳液及其膜性能的影响.结果表明,改性后的丙烯酸酯乳液具有良好的热稳定性.AA的加入,使乳液粒径减小,分布均匀,乳液稳定性较好,呈现假塑性流体性质.随着AA含量的增加,乳液黏度增大,胶膜拉伸强度增大,断裂伸长率减小,耐水性先提高后降低.当AA含量为2％时,乳液平均粒径为97.3 nm,胶膜吸水率从8.34％降至4.2％,力学性能优异,PVC与织物的粘接物的剥离强度从12.3 N/25mm提高到28.0 N/25mm.
参考文献
| [1] | 王亚茹,陈文钦,马敬红,杨曙光,徐坚.水性室温自交联聚丙烯酸酯乳液的制备及性能[J].高分子材料科学与工程,2012(08):9-13. |
| [2] | 张光华,王义伟,朱军峰,崔萌.核壳型自交联聚丙烯酸酯乳液的成膜性能[J].高分子材料科学与工程,2009(01):71-74. |
| [3] | 张娟,沈一丁,王海花,费贵强.酮肼交联对聚丙烯酸酯乳液及成膜性能的影响[J].功能材料,2013(02):194-196,201. |
| [4] | Minrui Li;Zhen Zheng;Shujuan Liu .Synthesis and properties of poly(acrylates-co-urethane) adhesives for low surface energy materials[J].International Journal of Adhesion & Adhesives,2011(6):565-570. |
| [5] | 费贵强,陈佳,沈一丁,王海花,王春雁.丙烯酸羟乙酯对自交联苯丙胶乳性能的影响[J].高分子材料科学与工程,2013(01):52-55,59. |
| [6] | Degrandi-Contraires, E.;Udagama, R.;Bourgeat-Lami, E.;McKenna, T.;Ouzineb, K.;Creton, C. .Mechanical properties of adhesive films obtained from PU-acrylic hybrid particles[J].Macromolecules,2011(8):2643-2652. |
| [7] | 王磊,赖小娟,黎晓茸,郭方元,谭俊领.酮肼交联及硅烷偶联水性聚氨酯乳液的流变行为[J].石油化工,2012(07):825-829. |
| [8] | 费贵强,陈宗明,沈一丁,王海花,朱科.GMA改性无溶剂阴离子聚氨酯/丙烯酸酯复合乳液的合成及性能研究[J].功能材料,2013(09):1257-1260. |
| [9] | Matthew P. Cashion;Taigyoo Park;Timothy E. Long .Influence of Hydrogen Bonding on the Adhesive Properties of Photo-Curable Acrylics[J].The Journal of Adhesion,2009(1/3):1-17. |
| [10] | Udagama, R.;Degrandi-Contraires, E.;Creton, C.;Graillat, C.;McKenna, T.F.L.;Bourgeat-Lami, E. .Synthesis of acrylic-polyurethane hybrid latexes by miniemulsion polymerization and their pressure-sensitive adhesive applications[J].Macromolecules,2011(8):2632-2642. |
| [11] | Minrui Li;Zhen Zheng;Shujuan Liu;Yuezeng Su;Wei Wei;Xinling Wang .Polyurethane (urea)/polyacrylates interpenetrating polymer network (IPN) adhesives for low surface energy materials[J].Polymers for advanced technologies,2012(7):1077-1083. |
| [12] | Yanjun Cui;Donghua Chen;Xinling Wang;Xiaozhen Tang .Crystalline structure in isocyanate reactive hot melt adhesives[J].International Journal of Adhesion & Adhesives,2002(4):317-322. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%