采用Gleeble-1500热模拟实验机研究2519铝合金高温变形组织演化行为.利用光学显微镜(OM)及透射电子显微镜(TEM)分析合金在不同压缩条件下的组织形貌特征.结果表明,2519铝合金在变形温度为300～450 ℃、应变速率为0.01～1 s-1条件下,仅发生动态回复;而在变形温度为350～450 ℃,变形速率为10 s-1的条件下变形时,发生动态再结晶,动态再结晶机制为连续动态再结晶和几何动态再结晶.
参考文献
| [1] | B. Carter Hamilton;Ashok Saxena .Transient crack growth behavior in aluminum alloys C415-T8 and 2519-T87[J].Engineering Fracture Mechanics,1999(1):1-22. |
| [2] | DEVINCENT S M;DEVLETIAN J H;GEDEON S A .Weld properties of the newly developed 2519-T87 aluminum armor alloy[J].Welding Journal,1988,67(07):33-43. |
| [3] | L.S. Kramer;T.P. Blair;S.D. Blough .Stress-Corrosion Cracking Susceptibility of Various Product Forms of Aluminum Alloy 2519[J].Journal of Materials Engineering and Performance,2002(6):645-650. |
| [4] | James J. Fisher Jr.;Lawrence S. Kramer;Joseph R. Pickens .ALUMINUM ALLOY 2519 IN MILITARY VEHICLES[J].Advanced Materials & Processes,2002(9):43-46. |
| [5] | 李慧中 .2519铝合金的合金化机理与性能研究[D].中南大学,2006. |
| [6] | 李慧中,张新明,陈明安,龚敏如,周卓平.2519铝合金焊接接头的组织与性能[J].中国有色金属学报,2004(06):956-960. |
| [7] | 陈险峰,彭大暑,张辉,林启权,林高用.热处理制度对2519铝合金板材力学性能和应力腐蚀敏感性的影响[J].中国有色金属学报,2003(04):934-938. |
| [8] | 沈健,唐京辉,谢水生.Al-Zn-Mg合金的热变形组织演化[J].金属学报,2000(10):1033-1036. |
| [9] | 李慧中,张新明,陈明安,周卓平.2519铝合金热变形流变行为[J].中国有色金属学报,2005(04):621-625. |
| [10] | 傅高升;陈文哲;钱匡武 .压力罐用铝材高温压缩变形的流变曲线特征[J].中国有色金属学报,2002,12(zk):140-145. |
| [11] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [12] | RAVICHANDRAN N;PRASAD Y V R K .Dynamic recrystallization during hot deformation of aluminium:A study using processing maps[J].Metallurgical and Materials Transactions,1991,22A(10):2339-2348. |
| [13] | OLLA P;VIRDIS P F .High temperature deformation of a commmercial aluminum alloy[J].Metallurgical and Materials Transactions,1987,18A(02):293-301. |
| [14] | HUMPHRYS F J;HATHERLY M.Recrystallization and related annealing phenomena[M].Pergamon Press,1955:363-483. |
| [15] | 沈健.AA7005铝合金的热加工变形特性[J].中国有色金属学报,2001(04):593-597. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%