通过干湿循环加速试验模拟Al表面沉积沙漠浮土情况下的大气腐蚀过程，利用失重分析、扫描电镜（SEM）和大气腐蚀监测仪（ACM）研究浮土中可溶性盐对Al的大气腐蚀的影响。结果表明：浮土中的可溶性盐会使发生大气腐蚀的相对湿度范围变宽，随着可溶性盐含量的提高，Al的腐蚀不断恶化。在可溶性盐成分中，MgCl2对Al的腐蚀影响最大，NaCl次之， MgSO4和Na2SO4的影响较小。
Atmospheric corrosion of aluminium deposited with desert dust was simulated using a laboratory-accelerated test of cyclic wet-dry. Effects of the soluble salts in desert dust on atmospheric corrosion of aluminium were studied through mass loss, scanning electron microscope (SEM) and atmosphere corrosion monitor (ACM). The results demonstrated that the soluble salts in dust can widen the scope of relative humidity in which atmospheric corrosion occurs. Atmospheric corrosion of aluminium was getting more seriously with the increasing of the salt content in desert dust. MgCl2 in desert dust had the strongest influence on atmospheric corrosion of aluminium, then did NaCl, MgSO4 and Na2SO4 had the smaller influence.
参考文献
| [1] | Xiao Y Q, Xie S S, Liu J A, et al. Practical Directory of Aluminium Alloys Technology [M]. Beijing: Metallurgical Industry Press, 2005[2](肖亚庆, 谢水生, 刘静安等. 铝加工技术实用手册 [M]. 北京: 冶金工业出版社, 2005)[3]Fuente D de la, Otero-Huerta E, Morcillo M. Studies of long-term weathering of aluminium in the atmosphere [J]. Corros. Sci., 2007,49(7), 3134-3148[4] Natesan M, Venkatachari G, Palaniswamy N. Kinetics of atmospheric corrosion of mild steel, zinc, galvanized iron and aluminium at 10 exposure stations in India [J]. Corros.Sci, 2006, 48(11):3584-3608 [5] Zhu H, Zheng Q F, Xie S S. Study on atmospheric corrosion of aluminium and its alloy at different distance away from sea shore in Wanning marine environment [J]. Rare Met, 2002, 26(6):456-459[6](朱红嫚, 郑弃非, 谢水生.万宁地区铝及铝合金不同距海点的大气腐蚀研究 [J]. 稀有金属, 2002,26(6): 456-459)[7]Wang Z Y, Yu G C, Han W. Atmospheric corrosion law of three nonferrous metals in Shenyang area [J]. Chin. J.Nonferrous. Met., 2003, 13(2)：367-372[8] 王振尧, 于国才, 韩薇. 3种有色金属在沈阳地区的大气腐蚀规律 [J]. 中国有色金属学报, 2003, 13(2):367-372 [9]Xiao Y D, Wang G Y, Li X G, et al. Corrosion behavior of atmospheric environment and corrosion feature of materials in our western area [J]. J. Chin. Soc. Corros. Prot.,2003, 23(4): 248-255[10] 萧以德, 王光雍, 李晓刚等. 我国西部地区大气环境腐蚀性及材料腐蚀特征 [J]. 中国腐蚀与防护学报, 2003, 23(4):248-255[11]Cao C N. Material Natural Environmental Corrosion of China [M]. Beijing: Chemical Industry Press, 2005: 69-73[12](曹楚南. 中国材料的自然环境腐蚀 [M]. 北京: 化学工业出版社, 2005: 69-73)[13] Bengtsson Blucher D, Svensson J E, Johansson L G. The influence of CO2, AlCl36H2O, MgCl2．6H2O,Na2SO4 and NaCl on the atmospheric corrosion of aluminum [J]. Corros. Sci, 2006, 48(7):1848-1866[14]Bengtsson Blucher D, Lindstrom R, Svensson J E, et al. The effect of CO2 on the NaCl-induced atmospheric corrosion of aluminum [J]. J. Electrochem. Soc., 2001, 148(4): B127-B131[15]Wan Y, Ren Y J, Yan C W. Effect of deposition of ammonium chloride and ammonium sulfate on atmospheric corrosion of LY12 alloy [J]. Chin. J. Nonferrous. Met., 2004, 14(7),1149-1155[16](万晔, 任延杰, 严川伟. 两种盐沉积对LY12铝合金大气腐蚀行为的影响 [J]. 中国有色金属学报，2004, 14(7), 1149-1155[17]Wang J. Role of salt particle deposition in the initiation and propagation of atmospheric corrosion [J]. J. Chin. Soc. Corros. Prot., 2004, 24(3): 155-158[18] 王佳. 无机盐微粒沉积和大气腐蚀的发生与发展 [J]. 中国腐蚀与防护学报, 2004, 24(3):155-158[19]Christofer Leygraf, Thomas Graedel. Han E H, et al Trans. Atmospheric Corrosion [M]. Beijing: Chemical Industry Press, 2005: 7-21(Christofer Leygraf, Thomas Graedel著. 韩恩厚等译. 大气腐蚀 [M]. 北京: 化学工业出版社, 2005: 7-21)[20]Marcus P, Oudar J. Corrosion Mechanism in Theory and Practice [M].Marcel Dekker, Inc., 1995[21] Elola A S, Otero T F, Porro A. Evolution of the pitting of aluminum exposed to the atmosphere [J]. Corrosion, 1992, 48(10):854-863[22] Pyun S I, Moon S M, Ahn S H, et al. Effects of Cl-, NO3- and SO4- ions on anodic dissolution of pure aluminium in alkaline solution [J]. Corros. Sci, 1999, 41:653-667[23] Graedel T E. Corrosion mechanisms for aluminium exposed to the atmosphere [J]. J. Electrochem. Soc, 1989, 136:204-212[24] Oesch S, Faller M. Environmental effects on materials: the effect of the air pollutants SO2, NO2, NO and O3 on the corrosion of copper, zinc and aluminum, a short literature survey and results of laboratory exposures [J]. Corros. Sci, 1997, 39:1505-[25] Rosa Vera, Diana Delgado, Blanca M Rosales. Effect of atmospheric pollutants on the corrosion of high power electrical conductors: Part 1Aluminium and AA6201 alloy [J]. Corros. Sci, 2006, 48:2882-2900[26] Arshadi M A, Johnson J B, Wood G C. The influence of an isobutene SO2 pollutant system on earlier stages of the atmospheric corrosion of metals [J]. Corros. Sci, 1983, 23:763-776 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%