利用扫描电镜和电子背散射衍射技术对冷拔高碳钢丝在600℃等温退火过程中再结晶织构的演变进行了研究，并且探究了织构强度与钢丝形变量及钢丝抗拉强度的关系。结果表明：再结晶织构继承了原来形变的〈110〉织构，并且随退火时间的延长，该织构强度先增加后减弱，并有〈112〉织构出现；形变量较大的钢丝其再结晶织构的强度也较高；钢丝的抗拉强度变化趋势与〈110〉织构强度的变化趋势有一定的对应关系。
The recrystallization texture evolution of cold drawn high carbon steel wire annealed at 600 ℃ was studied by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). The relations between texture intensity and deformation degrees and tensile strength of this steel wire were discussed. Results show that the recrystalization texture was the same as the 〈110〉 texture of drawn wires. The intensity of texture increased at first and then decreased with annealing time lengthened, and the 〈112〉texture appeared. When the cold drawn high carbon steel wire had a greater degree of deformation, the intensity of the reerystallization texture was higher. There was a corresponding relationship between the tensile strength of the steel wire and the intensity of 〈110〉 texture.
参考文献
| [1] | 王雷,涂益友,李凡,黄海波.冷拔高碳钢丝织构演变分析[J].东南大学学报（自然科学版）,2009(01):131-135. |
| [2] | 姚旭升,刘沿东,张正贵,蒋奇武,左良.冷拉拔纯铁丝在退火过程中的显微组织与织构演变[J].机械工程材料,2009(04):14-17,21. |
| [3] | Yandong LIU,Qiwu JIANG,Gang Wang,Yandong WANG,A.Tidu,Liang ZUO.Influence of Microstructures and Textures on the Torsional Behavior of Pearlitic Wires[J].材料科学技术学报（英文版）,2005(03):357-360. |
| [4] | 张晓丹,A．Godfrey,刘伟,刘庆.珠光体钢丝冷拉拔过程中微观组织及铁素体微区取向与织构演变[J].金属学报,2010(02):141-146. |
| [5] | 黄文长,冯继军.EBSD分析技术及其在材料科学研究中的应用[J].汽车工艺与材料,2004(01):18-20. |
| [6] | 杨平.EBSD技术在微织构分析中的应用[J].中国体视学与图像分析,2005(04):211-214,224. |
| [7] | Yasunobu NAGATAKI;Yoshihiro HOSOYA .Origin of the Recrystallization Texture Formation in an Interstitial Free Steel[J].ISIJ International,1996(4):451-460. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%