合成了全氢聚硅氮烷和硼氮烷的混杂先驱体并对其结构进行了表征;以混杂先驱体和3D碳纤维编制体为原料,采用先驱体浸渍-裂解(PIP)工艺制得了碳纤维增强氮化硼-氮化硅混杂基体的复合材料,并对复合材料的力学性能和抗烧蚀性能进行了研究.结果表明,混杂先驱体中含有B-N,B-H,Si-N,Si-H,N-H等结构,无其它杂质出现;随着PIP工艺循环次数的增加,复合材料的密度随之提高;当进行4个循环时基本致密,密度达到1.50g/cm3,弯曲强度达到156.4 MPa;轨道模拟实验显示复合材料具有优异的抗烧蚀性能.

参考文献

[1] Samah A;Paulmier D;Mansori M E.[J].Surface and Coatings Technology,1999(120-121):636.
[2] Lee Y-J;Joo H J.[J].COMPOSITES,2004(35A):1285.
[3] Manocha LM.;Patel KB.;Glogar P.;Manocha S. .Oxidation behaviour of carbon/carbon composites impregnated with silica and silicon oxycarbide[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(10):1481-1491.
[4] Lee YJ;Joo HJ .Ablation characteristics of carbon fiber reinforced carbon (CFRC) composites in the presence of silicon carbide (SiC) coating[J].Surface & Coatings Technology,2004(0):286-289.
[5] Seghi S;Fabio B;Economy J.[J].CARBON,2004(42):3043.
[6] Kim D P;Economy J.[J].CHEMISTRY OF MATERIALS,1993(05):1216.
[7] Cofer C G;Saak A W;Economy J.[J].Ceramic Engineering & Science Proceedings,1995(16):663.
[8] Seghi S;Lee J;Economy J.[J].CARBON,2005(43):2035.
[9] Hough W V;Guibert C R;Hefferan G T .Method for the synthesis of borazine[P].United States Patent,4150097,1979.
[10] Isoda T;Kaya H;Nishii H.[J].J Inorgan Organomet Poly,1992(02):151.
[11] Prelas M A;Benedictus A;Lin L S.Diamond Based Composites and Related Materials[M].Dordrecht,Netherlands:Kluwer Academic Press,1997
[12] 张巍,张博明,孟松鹤,韩杰才.细编穿刺碳/碳复合材料等离子火炬高温烧蚀性能研究[J].材料工程,2003(05):23-25.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%