采用表层组织超细化轧制工艺在首钢3 500 mm中厚板生产线上进行了L245管线钢板的批量试制.结果表明,采用这种特殊的控轧控冷工艺,普碳钢的化学成分可保证钢板的力学性能达到厚规格L245管线钢板的要求.试制钢板表层铁素体晶粒达到12级,中心部位10级,屈服强度达到300～365 MPa,抗拉强度达到430～480MPa,同时保持29%～35%的伸长率,-10℃夏比冲击功130 J以上,剪切面积85%以上.在几乎不增加冶金成本的前提下,试制钢板具有优良的强度、塑性配合,优良的低温韧性水平.
参考文献
| [1] | Hurley PJ;Muddle BC;Hodgson PD .Analysis and characterisation of ultra-fine ferrite produced during a new steel strip rolling process[J].Scripta materialia,1999(4):433-438. |
| [2] | 杨王玥,齐俊杰,孙祖庆,杨平.低碳钢形变强化相变的特征[J].金属学报,2004(02):135-140. |
| [3] | 翁宇庆.超细晶钢-钢的组织细化理论与控制技术[M].北京:冶金工业出版社,2003:521-556. |
| [4] | Hidesato MABUCHI;Toshiei HASEGAWA;Tadashi ISHIKAWA .Metallurgical Features of Steel Plates with Ultra Fine Grains inSurface Layers and their Formation Mechanism[J].ISIJ International,1999(5):477-485. |
| [5] | Ishikawa T.Steel Plate Having Surface-Layers With Ultrafine Grained Microstructure (SUF Steel) and Its Welding Joint Properties[A].Tsukuba,2002:91-92. |
| [6] | 范建文,谢瑞萍,张维旭,王彦锋,阎智平.表层超细晶粒普碳钢中厚板的工业试制[J].钢铁,2006(04):40-46,55. |
| [7] | Fan J W .Fatigue Behavior of Low Carbon Steel Plates With Fine Grained Ferrite in Surface Layers[J].Materials Science and Technology,2005,21(05):583-589. |
| [8] | Mintz B;姚泽雄;成光祜.微合金化低碳高强度钢[M].北京:冶金工业出版社,1982:51-57. |
| [9] | Ginzburg V B;马东清;陈荣清.板带轧制工艺学[M].北京:冶金工业出版社,1998:50-91. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%