采用硫酸阳极氧化法在LY12铝合金表面制备了阳极氧化膜,然后以γ-环氧丙氧丙基三甲氧基硅烷(GPTMS)/正硅酸乙酯(TEOS)杂化溶胶封闭,并在封闭过程中引入Ce3+作为缓蚀剂.对吸附Ce3+的铝合金阳极氧化膜进行了X射线光电子能谱(XPS)分析.通过极化曲线与电化学阻抗谱(EIS)研究了铈盐和硅烷杂化溶胶改性的阳极氧化铝合金电极在25℃C、3.5%(质量分数)NaCl溶液中的耐蚀长效性.结果表明,硅烷杂化溶胶封闭方法极大提高了阳极氧化膜的耐长期腐蚀性能.Ce3+在硅烷杂化溶胶封闭的阳极氧化膜体系中的引入方式不同导致其耐蚀长效性具有显著差异.吸附Ce3+后再经硅烷杂化溶胶封闭的阳极氧化膜电极的耐蚀性显著高于铈盐掺杂硅烷杂化溶胶封闭的阳极氧化膜.
参考文献
| [1] | 吴纯素.化学转化膜[M].北京:化学工业出版社,1986:6. |
| [2] | Correa-Borroel, AL;Gutierrez, S;Arce, E;Cabrera-Sierra, R;Herrasti, P .Organosilanes and polypyrrole as anticorrosive treatment of aluminium 2024[J].Journal of Applied Electrochemistry,2009(12):2385-2395. |
| [3] | 朱祖芳.铝合金阳极氧化与表面处理技术[M].北京:化学工业出版社,2010:224. |
| [4] | 周琦,贺春林,才庆魁,邵忠宝,朱学松.6种铝阳极氧化无铬封孔膜的性能比较[J].材料保护,2009(02):31-34. |
| [5] | Chou TP.;Limmer SJ.;Seraji S.;Wu Y.;Forbess MJ. Nguyen C.;Cao GZ.;Chandrasekaran C. .Organic-inorganic hybrid coatings for corrosion protection[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2001(2/3):153-162. |
| [6] | Metroke TL;Gandhi JS;Apblett A .Corrosion resistance properties of Ormosil coatings on 2024-T3 aluminum alloy[J].Progress in Organic Coatings: An International Review Journal,2004(4):231-246. |
| [7] | METROKE T L;APBLETT A .Effect of solvent dilution on corrosion protective properties of Ormosil coatings on 2024-T3 aluminum alloy[J].Progress in Organic Coatings,2004,51(01):36-46. |
| [8] | 张金涛,潘亮,李春东.LY12铝合金表面硅烷杂化膜的电化学性能研究[J].电镀与涂饰,2008(09):22-25. |
| [9] | Palanivel V;Huang Y;Ooij WJ .Effects of addition of corrosion inhibitors to silane films on the performance of AA2024-T3 in a 0.5M NaCl solution[J].Progress in Organic Coatings: An International Review Journal,2005(2):153-168. |
| [10] | A. M. Cabral;W. Trabelsi;R. Serra;M. F. Montemor;M. L. Zheludkevich;M. G. S. Ferreira .The corrosion resistance of hot dip galvanised steel and AA2024-T3 pre-treated with bis-[triethoxysilylpropyl] tetrasulfide solutions doped with Ce(NO_3)_3[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3740-3758. |
| [11] | 张金涛,杨春勇,潘亮,李春东.2A12铝合金表面铈盐掺杂硅烷杂化膜在3.5%NaCl溶液中耐蚀性能的电化学研究[J].金属学报,2008(11):1372-1377. |
| [12] | 张金涛,李春东,潘亮,胡吉明.铈盐掺杂GPTMS/TEOS硅烷杂化膜腐蚀电化学行为随时间的变化[J].腐蚀与防护,2009(12):879-882,908. |
| [13] | 赵景茂,陈胜利,赵旭辉,左禹.铈盐在电场作用下对LY12铝合金阳极氧化膜的封闭作用[J].中国表面工程,2008(01):28-32. |
| [14] | 李凌杰,雷惊雷,李荻,屈卫娟,张胜涛,潘复生.几种稀土盐封闭的铝阳极氧化试样的腐蚀行为[J].中国稀土学报,2007(01):64-68. |
| [15] | 王春涛,林伟国,曹华珍,郑国榘.含稀土介质中铝合金阳极氧化研究[J].表面技术,2003(03):49-51. |
| [16] | 杨胜奇.稀土在金属表面处理工艺中的应用技术（7）--稀土铝及其合金宽温耐蚀耐磨硫酸阳极氧化工艺技术[J].材料保护,2008(09):72-74. |
| [17] | 李国强,李荻,李久青,郭宝兰,彭明霞.铝合金阳极氧化膜上阴极电解沉积的稀土铈转化膜[J].中国腐蚀与防护学报,2001(03):150-157. |
| [18] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004:251. |
| [19] | 曹楚南;张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002:156-164. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%