通过热力学平衡相计算方法并采用相应的Ni基数据库,对1种新型高铬的Ni-Cr基GH648合金成分对平衡相析出的影响规律进行系统研究.结果认为GH648合金析出的主要平衡相为a-Cr,γ相和M23C6碳化物(主要为Cr23C6),并进一步计算了合金成分对这些相的析出行为及合金初熔点和终熔点的影响规律.计算结果表明,Cr含量主要影响a-Cr的析出量及开始析出温度,并影响合金的初熔点,对以Cr为主的M23C6的析出行为没有明显影响.C显著影响碳化物的析出量,而Al,Ti增加显著增加γ相的析出量和开始析出温度.
参考文献
| [1] | Radavich J.Superalloy 718, 625, 706 and Various Derivatives[J].TMS,1996:409. |
| [2] | 董建新;张麦仓;曾燕屏 et al.[J].Journal of University of Science and Technology Beijing(English Edition),2002,24:186. |
| [3] | Shen G;Radavich J;Xie X;Lindsley B.Superalloy 2000[J].The Journal of Microcolumn Separations,2001:445. |
| [4] | 王改莲,吴翠微,张麦仓,董建新,谢锡善.α-Cr在Incone1718合金中析出行为的微观分析[J].稀有金属材料与工程,2002(01):37-40. |
| [5] | Lindsley B;Pierron X;Maurer G.Long Time Stability of High Temperature Materrals[M].Now York:The Minerals,Metals & Materials Society,1999:123. |
| [6] | Gale W F;Abdo Z A M;Nemani R V .[J].Journal of Materials Science,1999,34:407. |
| [7] | Ustinovshikov Y .[J].Acta Materialia,1996,44:5021. |
| [8] | Marucco A .[J].Materials Science and Engineering,1995,A194:225. |
| [9] | 颜晓峰,马惠萍,卢亚轩,刘万生.Cr含量对GH648合金组织及力学性能的影响[J].材料工程,2002(03):28-31. |
| [10] | 颜晓峰;马惠萍;卢亚轩 .Material Engineering[J].材料工程,2002,3:28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%