高磁粉装载量PPS/NdFeB注射磁体的制备是目前国内外研究的重点.成功制备出磁粉装载量90％(质量分数)左右的PPS/NdFeB粘结磁体以及可实际应用永磁元器件,应用DSC、SEM和磁化曲线测量仪等表征了注射磁体微观结构和磁性能,并分析注射温度、速度和压力等工艺参数对粘结磁体微观结构和磁性能的影响规律和机理,结果表明,当注射温度为305℃、注射速率为90％Vmax、注射压力为153MPa时,粘结磁体((φ)10mm×10mm)密度可达5.12g/cm3,磁性能可达(BH)max=47.1kJ/m3,Br=0.53T,Hci=647.3kA/m,粘结永磁元器件(外径(φ)20mm,内径(φ)18mm)24极充磁后,表面磁场强度达到145.06mT.
参考文献
| [1] | Song Dayu;Liu Ying et al.[J].Journal of Functional Materials,2005,36(09):1337-1340. |
| [2] | Duan Bohua;Qu Xuanhui;Li Yunping et al.[J].Journal of Magnetic Materials and Devices,2003,12(04):36-39. |
| [3] | Campbell P.Permanent Magnet Materials and their Application[M].Cambridge:Cambridge University Press,1994 |
| [4] | Furlani E P.Permanent Magnet and Electromechanical Devices:Materials,Analysis,and Applications[M].New York:Academic Press,Inc,2001 |
| [5] | Garrell M G;Shih A J;Ma B M et al.[J].Magnetism and Magnetic Materials,2003,25(07):32-43. |
| [6] | Garrell M G;Shih A J;Ma B M et al.[J].Magnetism and Magnetic Materials,2003,35(09):375-383. |
| [7] | Ma BM.;Herchenroeder JW.;Smith B.;Suda M.;Brown DN.;Chen Z. .Recent development in bonded NdFeB magnets[J].Journal of Magnetism and Magnetic Materials,2002(1/3):418-423. |
| [8] | 张小磊,朱明原,李瑛,金红明,田野,王谆,杨秋平.粘结剂和添加剂对注射成型各向异性粘结NdFeB磁体的影响[J].稀有金属材料与工程,2008(11):1978-1981. |
| [9] | 刘冬,邹科,熊凌云.注射成形各向异性粘结NdFeB磁体工艺参数的研究[J].矿冶,2009(01):60-63. |
| [10] | 段柏华,曲选辉,邹黎明,徐征宙,郭世柏.工艺参数对注射成形各向异性粘结NdFeB磁体性能的影响[J].粉末冶金技术,2005(05):352-355. |
| [11] | 李益民,黄伯云,曲选辉.金属注射成形技术进展[J].稀有金属材料与工程,1996(01):1-4. |
| [12] | 段柏华 .高性能注射成形各向异性Nd-Fe-B粘结磁体的研究[D].中南大学,2005. |
| [13] | 李益民,黄伯云,钟伟.工艺参数对金属注射成形坯缺陷的影响[J].稀有金属材料与工程,1999(02):117-120. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%