The feasibility of fabricating ZL104 aluminum alloy with non-dendritic microstructure by semi-solid isothermal heat treatment process and the effects of holding temperature and time on the semi-solid isothermal heat-treated microstructure of the alloy, are investigated. The research results indicate that it is possible to produce ZL104 alloy with non-dendritic microstructure by a suitable semi-solid isothermal heat treatment. After treated at 580 ℃ for 120 min, the ZL104 alloy can obtain a non-dendritic microstructure with an 49% liquid content and an average size range of 115 μm of the unmelted primary solid particles. In addition, an increase in the holding time from 30 to 120 min for a given holding temperature of 580 ℃ or in the holding temperature from 570 to 580 ℃ for a given holding time of 120 min causes the average size and globular tendency of unmelted primary solid particles in the semi-solid ZL104 alloy to decrease and become more obvious, respectively.

参考文献

[1] Du X H;Zhang E L .[J].Materials Letters,2007,61:2333.
[2] Flemings M C .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22:957.
[3] Chen T J;Ma Y;Hao Y et al.[J].Transactions of Nonferrous Metals Society of China,2001,11:98-102.
[4] Chen T J;Hao Y;Sun J et al.[J].Science and Technology of Advanced Materials,2003,4:495.
[5] Kim J M;Kim K T;Jung W J .[J].Materials Science and Technology,2002,18:698.
[6] Bai B Z;Li J G;Zheng Y K .[J].Rare Metals,2002,21(03):224.
[7] Li J G;Ma H T;Zhang B Q et al.[J].Acta Metallurgica Sinica,2000,39(06):579.
[8] Wang J L;Su Y H;Tsao C Y A .[J].Scripta Materialia,1997,37:2003.
[9] Czerwinski F .The processing phenomena of semisolid Mg-9% Al-1% Zn alloy at ultra high contents of the unmelted phase[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):51-61.
[10] Zhang Q Q;Cao Z Y;Zhang Y F et al.[J].Journal of Materials Processing Technology,2007,184:195.
[11] Lashkari O;Nafisi S;Langlais J et al.[J].Journal of Materials Processing Technology,2007,182:95.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%