对于采用某种有机涂料封孔处理的电弧喷涂铝涂层,采用电化学阻抗谱(EIS)、扫描电镜(SEM)和能谱(EDS)分析并结合划格试验,研究了封孔铝涂层在盐雾条件下腐蚀防护性能.结果表明,封孔电弧喷涂铝涂层很快腐蚀,但经过2 400 h盐雾加速试验(SST)后仍能对基体提供牺牲阳极保护;反应生成的铝离子可以通过封孔层孔隙渗透至面漆涂层表面并最终生成白絮状产物;根据EIS结果提出了相应的特征等效电路;SST后封孔涂层与喷涂层结合仍然良好.
参考文献
| [1] | 周林玉,刘莹,邵英平,李建敏.热喷涂涂层封孔材料及其耐酸蚀性能[J].热喷涂技术,2009(02):39-42,70. |
| [2] | 于惠博,王亚昆,孙宏飞,武彬,刘美淋.降低热喷涂涂层孔隙率的方法[J].新技术新工艺,2006(11):15-18. |
| [3] | H. Marchebois;M. Keddam;C. Savall;J. Bernard;S. Touzain .Zinc-rich powder coatings characterisation in artificial sea water EIS analysis of the galvanic action[J].Electrochimica Acta,2004(11):1719-1729. |
| [4] | Liu, XW;Xiong, JP;Lv, YW;Zuo, Y .Study on corrosion electrochemical behavior of several different coating systems by EIS[J].Progress in Organic Coatings,2009(4):497-503. |
| [5] | Linda G. S. Gray;Bernard R. Appleman .EIS: electrochemical impedance spectroscopy a tool to predict remaining coating life?[J].Journal of Protective Coatings & Linings,2003(2):66-74. |
| [6] | 刘美淋,孙宏飞,于惠博,武彬.降低热喷涂涂层孔隙率的方法[J].腐蚀与防护,2007(04):171-173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%