对C-Si-Mn冷轧低碳钢进行了淬火与配分(Q&P)处理.利用热膨胀仪、光学显微镜、扫描电镜、电子万能试验机、X射线衍射等实验手段,研究了实验钢奥氏体化温度和奥氏体化保温时间对相变组织的影响,并探讨了显微组织和力学性能随Q＆P工艺中配分温度和配分时间等工艺参数的变化规律.结果表明,Q&P配分温度和配分时间强烈影响最终残留奥氏体含量.本实验中最佳配分工艺下,残留奥氏体量(体积分数)可以达到10％以上,从而使试验钢具有良好的强塑积.其伸长率约15.5％,抗拉强度为1352 MPa,强塑积可达到21000 MPa·％以上.
参考文献
| [1] | Horvath C D;Fekelc J R.Opportunities and challenges for increased usage of advanced high strength steels in automobile applications[A].AIST Golden CO,USA,2004:1-7. |
| [2] | 唐荻,米振莉,陈雨来.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005(06):1-5. |
| [3] | Takehide SENUMA .Physical Metallurgy of Modern High Strength Steel Sheets[J].ISIJ International,2001(6):520-532. |
| [4] | Wenquan Cao;Cunyu Wang;Jie Shi;Han Dong.Application of Quenching and Partitioning to Improve Ductility of Ultrahigh Strength Low Alloy Steel[J].Materials Science Forum,2010:29-32. |
| [5] | D.V. Edmonds;K. He;E.C. Rizzo .Quenching and partitioning martensite--A novel steel heat treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(0):25-34. |
| [6] | Mi Z L;Tang D;Yan L et al.High strength and high plasticity TWIP steel for model vehicle[J].Materials Science and Technology,2005,21(04):24-27. |
| [7] | 庄宝潼,唐荻,江海涛,刘智.Q＆P工艺对0.3C-1.35Mn-1.30Si钢力学性能的影响[J].材料热处理学报,2011(11):34-38. |
| [8] | J. Speer;D. K. Matlock;B. C. De Cooman;J. G. Schroth .Carbon partitioning into austenite after martensite transformation[J].Acta materialia,2003(9):2611-2622. |
| [9] | Speer JG;Edmonds DV;Rizzo FC;Matlock DK .Partitioning of carbon from supersaturated plates of ferrite, with application to steel processing and fundamentals of the bainite transformation[J].Current opinion in solid state & materials science,2004(3/4):219-237. |
| [10] | Speer J G;Rizzo F C;Matlock D K et al.The "quenching and partitioning" process:Background and recent progress[J].Materials Research,2005,8(04):417-423. |
| [11] | 徐祖耀.钢热处理的新工艺[J].热处理,2007(01):1-11. |
| [12] | Andrew K W .Empirical formulae for the calculation of some transformation temperature[J].Iron Steel Inst,1965,203(07):721-727. |
| [13] | M. De Meyer;J. Mahieu;B. C. De Cooman .Empirical microstructure prediction method for combined intercritical annealing and bainitic transformation of TRIP steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(10):1121-1132. |
| [14] | Speer J G;Streicher A M;Matlock D K.Quenching and partitioning:a fundamentally new process to create high strength TRIP sheet microstructures[A].Warrendale,PA,USA:TMS/ ISS,2003:505-522. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%