A rapid and more efficient method was developed to prepare nucleus/shell titania/hydroxyapatite (TiO2/HAP)complex nanophotocatalyst. Hydroxyapatite (5μm) which had been dissolved with 0.1 mol/L HCI was formed on the surface of the nanosized anatase titania powders by increasing the pH value of the solution at 90℃ in the water bath for only several hours .The microstructure and morphology of the resulting sample were investigated by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy dispersive spectrum (EDS) and atomic force microscope (AFM). The results indicated that nucleus/shell structural TiO2/HAP was formed in our experiments, and the thickness of the coating layer was about 5 nm. Photocatalytic decomposition of methyl orange was utilized to test the photocatalysis of the resulting samples and the result was compared with that of pure anatase titania powders (about 20 nm). It was shown that the photocatalytic activity of the sample was not decreased due to the coating of HAP.
参考文献
| [1] | W F Libby .[J].Science,1971,171:499. |
| [2] | A Fujishima;K Kohayakawa .[J].Journal of The American Chemical Society,1975,122:1487. |
| [3] | L D Birkefild;A M Azad;S A Akbar .[J].Journal of the American Chemical Society,1992,75:2964. |
| [4] | B O'Regan;M Gratzel .[J].Nature,1991,353:737. |
| [5] | N M Lawandy;R M Balachandran;A S L Gomes;E Sauvaln .[J].Nature,1994,368:436. |
| [6] | M R Hoffmann;S T Martin;W Choi;D W Bahnemann .[J].Chemical Reviews,1995,95:69. |
| [7] | A Fujishima;K Honda .[J].Bulletin of the Chemical Society of Japan,1971,44:1148. |
| [8] | A Fujishima;K Honda .[J].Nature,1972,238:37. |
| [9] | V.A.Sakkas;I.M.Arabatzis;I.K.Konstantinou;A.D.Dimou;T.AAlbanis;P.Falaras .Metolachlor photocatalytic degradation using TiO_2 photocatalysts[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2004(3):195-205. |
| [10] | Lin X Chen;Tijana Rajh;Zhiyu Wang;David M Tiede and Marion Thurnauer .[J].Nuclear Instruments & Methods In Physics Research Section B-beam Interact,1997,133(08) |
| [11] | Jean-Marie Herrmann .[J].Catalysis Today,1999,53:115. |
| [12] | Hebin Shi;Yu Liu;Hong Zhong .[J].Chem Bioeng,2003,6:48. |
| [13] | S Tsuru;N Shinomiya;Y Katsura;Y Uwabe,M Noritate and M Rokutanda .[J].Bio-medical Materials and Engineering,1991,1:143. |
| [14] | A Tiselius;S Hjerten;O Levin .[J].Archives of Biochemistry and Biophysics,1956,65:156. |
| [15] | T Nonami;H Taoda;N T Hue;E Watanabe,K Iseda,M Tazawa and M Fukaya .[J].Materials Research Bulletin,1998,33:125. |
| [16] | Hirotaka Maeda;Toshihiro Kasuga;Masayuki Nogami .[J].Journal of the European Ceramic Society,2004,24:2125. |
| [17] | Toshihiro Kasuga;Hayato Kondo;Masayuki Nogami .[J].Journal of Crystal Growth,2002,235:235. |
| [18] | Mei Wei;Masaki Uchida;Hyun Min Kim .[J].Biomaterials,2002,23:167. |
| [19] | Juan Yang;Dan Li;Xin Wang;Xujie Yang and Lude Lui .[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,2002,328(108) |
| [20] | Lianfeng Guo,Wenguang Zhang,Chengtao Wang.Preparation and crystallization control of nanoparticle hydroxyapatite[J].北京科技大学学报(英文版),2004(05):449-454. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%