研究了双层辉光放电条件下镍基合金Inconel 625的阴极溅射行为。 结果表明: 多组元镍基合金由于各组元溅射率不同, 产生择优溅射现象。 Mo, Nb等低溅射率元素在阴极表面富集, Ni, Cr等高溅射率元素在阴极表面贫化, 使阴极表面发生相变, 形成含Mo, Nb较高的金属间化合物析出相P相和Laves相。 随着阴极溅射电压的增加, 阴极合金元素溅射率增加; 并且随着阴极温度升高, 阴极溅射率也随之增加。

The cathode sputtering of nickel base alloy Inconel 625 was studied in double glow discharge. The results show that the preferential sputtering effect is happened in Ni-Cr-Mo-Nb alloy as the deference of element sputtering rates. The content of lower sputtering rate elements Mo and Nb increases while the higher sputtering rate elements Ni and Cr decrease in the surface layer, and the intermetallic phases P and Laves containing high concentration of Mo and Nb precipitate in surface layer. The sputtering rate increases with the increase of the cathode voltage and the temperature.

参考文献

[1] Greene J E .Sputtering of metal alloy containing second-phase precipitates[J].Journal of Applied Physics,1978,49(01):417.
[2] 任建世 .镍基合金辉光放电阴极溅射表面形貌[J].金属学报,1989,25(04):B288.
[3] Xu Zhong .Method and Appuratus for Introducting Normally Solid Materials Into Substrate Surface[P].US:4520268
[4] 徐 重;王振民;古风英.双层辉光离子渗金属[J].金属热处理学报,1982(02):71.
[5] 李成明,贺志勇,徐重.离子钨钼共渗的扩散机制[J].中国有色金属学报,2000(02):185.
[6] 张旭;董建新;杨忠民.双层辉光离子渗镍基合金表面合金化的研究[J].金属学报,1999(z2):505.
[7] Xu Zhang,Zhongmin Yang,Jianxin Dong,Xishan Xie,Yuan Gao,Zhong Xu.Surface Metallurgy of Nickle Base Superalloy[J].北京科技大学学报(英文版),1999(01):47-49.
[8] 徐 重.双层辉光离子渗金属技术[J].太原工业大学学报(自然科学版),1993(z1):60.
[9] 贺志勇;古风英;徐 重.双层辉光离子镍铬共渗最佳工艺参数的研究[J].金属热处理学报,1990(03):64.
[10] 王从曾;徐 重;苏永安.不等电位空心阴极放电特性的研究[J].太原工业大学学报(自然科学版),1991(12):3.
[11] 王从曾;唐 宾;苏永安.不等电位空心阴极离子渗金属工艺特性及其应用[J].金属热处理学报,1991(03):43.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%