研究了添加0～20%Al2O3(质量分数,下同)的3Y-TZP/Al2O3复相陶瓷在300℃空气环境下退火处理的相变行为,并考察了复相陶瓷的抗弯强度、断裂韧性等力学性能退火处理前后的变化,对相变机理进行了分析.结果表明:Al2O3可以有效抑制退火处理过程中氧化锆t→m相变,当Al2O3含量为6%即有明显的抑制效果,而且具有较优的综合性能.
参考文献
| [1] | Simon L .[J].Fur Ceram Soc,1995,15(06):485. |
| [2] | Lange F F;Dunlop G L;Davis B I .[J].Journal of the American Ceramic Society,1986,69(03):327. |
| [3] | Sato T;Shimada M .[J].Journal of the American Ceramic Society,1985,68(06):356. |
| [4] | Yoshimura M et al.[J].Journal of Materials Science Letters,1987,6(04):465. |
| [5] | Schmaudcr S;Schubert H .[J].Journal of the American Ceramic Society,1986,69(07):534. |
| [6] | Theunissen G S A M;Winnubst A J A;Burggraaf A J .[J].Journal of the European Ceramic Society,1992,12(09):251. |
| [7] | Sato T;Shimada M .[J].Proc Br Ceram Soc,1986,37:151. |
| [8] | Boutz MMR.;Vanlangerak B.;Scholtenhuis RJMO.;Kreuwel K. Burggraaf AJ.;Winnubst AJA. .THE EFFECT OF CERIA CO-DOPING ON CHEMICAL STABILITY AND FRACTURE TOUGHNESS OF Y-TZP[J].Journal of Materials Science,1995(7):1854-1862. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%