在可聚合乳化剂甲基丙烯磺酸钠存在下,以过硫酸钾和亚硫酸氢钠为氧化还原引发体系,将苯乙烯和N-异丙基丙烯酰胺进行无皂乳液聚合,制得粒径大小在200 nm~300 nm范围内的单分散热敏性聚(苯乙烯/甲基丙烯磺酸钠/N-异丙基丙烯酰胺)微球.通过透射电镜观察微球形态和大小,并采用激光光散射粒度仪考察微球粒径大小随温度变化情况.探讨了水溶性单体/油溶性单体比、引发剂用量等对微球粒径大小的影响.结果表明,制备的乳胶粒粒径在32℃附近明显减小,呈现出热敏性质;微球粒径随水溶性单体/油溶性单体比的增大而减小,随引发剂用量的增大而增大.
参考文献
[1] | Gao J.;Wu C. .THE COIL-TO-GLOBULE TRANSITION OF POLY(N-ISOPROPYLACRYLAMIDE) ON THE SURFACE OF A SURFACTANT-FREE POLYSTYRENE NANOPARTICLE[J].Macromolecules,1997(22):6873-6876. |
[2] | 丁小斌,孙宗华,万国祥,江英彦.热敏性磁性高分子微球同蛋白质的相互作用[J].高分子学报,2000(01):9-13. |
[3] | Lee CF;Wen CJ;Lin CL;Chiu WY .Morphology and temperature responsiveness-swelling relationship of poly(N-isopropylamide-chitosan) copolymers and their application to drug release[J].Journal of Polymer Science, Part A. Polymer Chemistry,2004(12):3029-3037. |
[4] | Chen CW.;Akashi M.;Tano D. .Colloidal platinum nanoparticles stabilized by vinyl polymers with amide side chains: Dispersion stability and catalytic activity in aqueous electrolyte solutions[J].Journal of Colloid and Interface Science,2000(2):349-358. |
[5] | Deng ZW;Hu XX;Li L;Xu ZS;Yi CF .Self-assembled poly(styrene-co-N-isopropylacrylamide) film induced by capillary force[J].Journal of Applied Polymer Science,2006(6):3514-3519. |
[6] | Yi CF;Xu ZS .Synthesis and characterization of thermosensitive composite microsphere latex[J].Journal of Applied Polymer Science,2005(3):824-828. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%