The graphitization behavior of ultrahigh carbon steels containing Si in hot rolling processes was investigated. The graphite stringers went mostly through the small pores and generally paralleled to the rolling direction. The influence of alloy elements on graphitization was estimated based on thermodynamics, which showed that Si content was important for graphitization. Graphite stringers nucleated at small pores and grew with carbon diffusion during hot rolling. Alloy contents, pores and hot deformation at γ+Fe3C phase range were the key factors for the formation of graphite. The probable effect of deformation on graphite formation during hot rolling was discussed in this paper.