研究了Ti和C添加对Nd9.4Fe79.6-xTixB11-yCy(x=0,1,2,4,6;y=0.5,1.5,3)合金晶化方式、显微结构和磁性能的影响规律.结果表明,适量Ti和C添加改变了合金的晶化方式,使α-Fe相和Nd2Fe14B相同时从Nd9.4Fe75.6Ti4B10.5C0.5非晶基体中析出,避免了先析出相晶粒的长大,利于获得细小均匀的显微结构.适量Ti和C添加的Nd-Fe-B-Ti-C非晶合金在退火过程中易析出细小弥散的TiC和TiB2相,可作为形核质点促进形核,且可抑制晶粒长大,最终形成细小均匀的显微结构.综合性能较佳的Nd9.4Fe75.6Ti4B10.5C0.5合金退磁曲线具有优异的方形度,最佳退火条件下合金薄带的剩磁Br为0.91 T,矫顽力iHc为976 kA·m-1,磁能积(BH)max达135 kJ·m-3.文章最后对Ti和C添加合金微结构的形成机制进行了探讨.
参考文献
| [1] | Manaf A;Bucldey R A;Davies H A .New nanocrystalline high remanence Fe-Nd-B alloys by rapid solidification[J].Jonrnal of Magnetism and Magnetic Materials,1993,128:307. |
| [2] | Yang S;Li S D;Liu X S;Song X P .Exchange coupled Nd2Fe14B/α-Fe nanocompesite magnets with fine α-Fe gains ob-tained by low wheel speed spinning[J].Journal of Alloys and Compounds,2002,343:217. |
| [3] | Coehoorn R;DeMooij D B;DeWanrd C .Melt spun permanent magnet materials containing Fe3B as the main phase[J].Journal of Magnetism and Magnetic Materials,1989,80:101. |
| [4] | Hirosawa S;Shigemoto Y;Miyeshi T;Kanckiyo H .Direct formarion of Fe3B/Nd2Fe14 B nanocomposite permanent magnets in rapid solidification[J].Scripta Materialia,2003,48:839. |
| [5] | You C Y;Ping D H;Hono K .Magnetic properties and microstructure of Fe3B/Pr2Fe14B-type nanocompesite magnets with Co and Cr additions[J].Journal of Magnetism and Magnetic Materials,2006,299:136. |
| [6] | Chen Z M;Wu Y Q;Kramer M J .A study on the role of Nb in melt-spun nanocrystalline Nd-Fe-B magnets[J].Journal of Magnetism and Magnetic Materials,2004,268:105. |
| [7] | 吴义生,倪建森,徐晖,王震,周邦新,黄照华.Nd10.1Fe（83.7-x-y）CoxZryB6.2永磁材料结构和磁性能的研究[J].中国稀土学报,2005(03):295-298. |
| [8] | Chiriac H.;Castano FJ.;Marinescu M. .Nd8Fe73Co5Hf2B12 strip cast alloy[J].Journal of Applied Physics,2000(9 Pt.2):5338-5340. |
| [9] | Betancourta I;Davies H A .Enhanced coercivity in B-rich nanocompoeite α-Fe/(Nd,Pr)2Fe14B/Fe3B hard magnetic alloys[J].Applied Physics Letters,2005,87:162516. |
| [10] | Harrison N J;Davies H A;Todd I .Nd2Fe14B-based nanocompesite magnets with transition metal and carbon additions[J].Journal of Applied Physics,2006,99:08B504-08B501. |
| [11] | Hirosawa S;Kaneklyo H;Miyoshi T .Unusual effects of Ti and C additions on structural and magnetic properties of Nd-Fe-B nanocomposite magnets in a B-rich and Nd-poor composition range[J].Journal of Magnetism and Magnetic Materials,2004(1):58-67. |
| [12] | Nagahama D;Ohkubo T;Miyoshi T;Hirosawa S Hono K .Effect of Ti and C additions on the microstructure and magnetic properties of Nd6Pr1Fe80B13 melt-spun ribbons[J].Acta Materialia,2006,54:4871. |
| [13] | Branagan D J;McCallunm R W .Precipitation phenomenon in stoichiometric Nd2Fe14B alloys modified with titanium and titanium with carbon[J].Journal of Alloys and Compounds,1995,230:67. |
| [14] | Daniil M;OkumuraH;Hadjipanayis GC;Sellmyer D J .Effect of carbon substitution on the magnetic properties of Nd-Fe-(B,C) nanocompesite magnets[J].Journal of Magnetism and Magnetic Materials,2003,267:316. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%