NiAl金属间化合物的快速凝固组织

材料研究学报, 1996, 10(3): 267-270.

NiAl金属间化合物的快速凝固组织

上海交通大学

基金项目: 国家自然科学基金；上海市科委科技基金

关键词： NiAl , null , null

THE MORPHOLOGY OF RAPIDLY SOLIDIFIED NiAl INTERMATALLICS

SUN Baode(Shanghai Jiaotong University)YANG Gencang , ZHOU Yaohe , LIN Dongliang (Northwesten Polytechnical Univerity)(Shanghai Jiaotong University)(Correspondent:SUN Baode , Dept.Of Materials Engineering

Keywords： : NiAl rapid solidification needle-like crustal , 快速凝固 , 针状晶

用单辊快速凝固法制备了Ni原子分数为0.53—0.60的Ni-Al金属间化合物薄带,研究了成分与微观组织的关系.发现试样均为B2型单相Nial,Ni_(0.53)Al_(0.47)的快速凝固组织为10μm左右的等轴晶.Ni_(0.56)Al_(0.44)—Ni_(0.6)Al_(0.4)的组织分别为5μm左右的不规则和规则柱状晶.发现近理想配比的NiAl在快速凝固时形成计状晶亚结构.

The ribbons of Ni0.53 Al0 .47 Ni0.6 Al0.4 intermatallic compounds have been prepared by single roller rapidly solidified technology.Their composition and morphology have been investigated.TEM shows that the ribbons have the B2 structure;SEM shows that the

参考文献

[1]

SchulsonEM,BakerDR．ScriptaMet,1983,17:5192GaydoshDJ,JechRW,TitranRH．JofMaterSciLett,1985,4:1383孙宝德．合金化与快速凝固对NiAl金属间化合物的增塑研究,[博士论文],西北工业大学,19939．西安4KurzW,FisherDG著,毛协民等译,凝固原理,西安:西北工业大学出版社,1987:695MuffinsWW,SekerkaRF．JApplPhys,1964,35:4446SoffaWA,LaughlinDE．inAaronsonHIetaleds．Solid—solidPhaseTransformations．ASM,Pittsburgh,Pennsylvania,1981:159j

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网