研究了Fe73．5Cu1Nb3Si13．5B9纳米晶合金在0．1mol／L的NaCl溶液中的耐腐蚀性能，及对其软磁性能的影响。实验结果表明，Fe73．5Cu1Nb3Si13．5B9纳米晶合金经0．1mol／L的NaCl溶液腐蚀后溶液中有橙色沉淀物产生，XRD测试表明铁基纳米晶合金腐蚀后仍保留非晶纳米晶双相结构；铁基纳米晶合金有效磁导率口。随腐蚀时间的增加而降低，腐蚀30d后在频率为50Hz、1、100kHz时其有效磁导率μc较腐蚀前分别下降35．9％、35．3％、27．6％，矫顽力Hc由腐蚀前的0．7097A／m增加到1．117A／m，增加了57．4％，磁滞损耗Pu由腐蚀前的1．819J／m^3增加到2．994J／m^3，增加了64．6％，腐蚀后铁基纳米晶合金软磁性能有所下降。
The corrosion resistance of Fe73. sCu1Nb3Si13.5B9 nanocrystalline alloys in 0. 1mol/L NaCl solution and its influence to soft magnetic properties were studied. The results show that an orange precipitate was produced in the NaCl solution after corrosion, X-ray diffraction show that Fe-based nanocrystalline alloys retain amorphous-nanocrystalline duplex structure after corrosion; the effective permeability of Fe-based nanocrystalline alloys reduce with increasing of corrosion time, after corrosion for 30d, the effective permeability decreased by 35.9%, 35. 3% and 27. 6% at 50Hz, 1 and 100kHz, respectively, coercive force increase from 0. 7097 to 1.117A/m, increased by 57.4%, hysteresis loss increase from 1. 819 to 2. 994J/m^3 , increased by 64.6%, the soft magnetic properties of Fe-based nanocrystalline alloys are decreased after corrosion.
参考文献
| [1] | Yoshizawa Y;Oguma S;Yamauchi K .Fe-based soft magnetic alloys composed of ultrafine grain structure[J].Journal of Applied Physics,1988,64:6044. |
| [2] | Manjura Hoque S;Hakim M A;Khan F A et al.Ultra- soft magnetic properties of devitrified FeT,Cu0.6Nba4SilaB8.alloy[J].Materials Chemistry and Physics,2007,101(01):112-117. |
| [3] | Shahria F;Beitollahia A;Shabestaria S G et al.Struc- tural characterization and magnetoimpedance effect in amorphous and nanocrystalline A1Ge-substituted FeSiB- NbCu ribbons[J].Journal of Magnetism and Magnetic Materials,2007,312:35-42. |
| [4] | Yin Lei;Zhu Zhenghou;Zheng Haijuan et al.Coating on FeT8 Si9 Bla amorphous alloy magnetic core and its soft magnetic properties[J].Journal of Functional Materials,2012,43(06):722-724. |
| [5] | D. Szewieczek;A. Baron .Electrochemical corrosion properties of amorphous Fe_(78)Si_(13)B_9 alloy[J].Journal of Materials Processing Technology,2004(0):442-445. |
| [6] | Zhou PH;Xie JL;Liu YQ;Deng LJ .Composition dependence of microstructure, magnetic and microwave properties in ball-milled FeSiB nanocrystalline flakes[J].Journal of Magnetism and Magnetic Materials,2008(24):3390-3393. |
| [7] | D. Szewieczek;A. Baron;G. Nawrat .Electrochemical behavior of Fe_(78)Si_9B_(13) alloy in sulphate and chloride solution[J].Journal of Materials Processing Technology,2006(1/3):411-415. |
| [8] | Pardo A;Otero E;Merino M C et al.The influence of Cr addition on the corrosion resistance of Fe73.sSila,sBgNbaCul metallic glass in marine environ- ments[J].Corrosion Science,2002,44(06):1193. |
| [9] | V. Cremaschi;I. Avram;T. Perez .Electrochemical studies of amorphous, nanocrystalline, and crystalline FeSiB based alloys[J].Scripta materialia,2002(1):95-100. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%