采用ODF织构分析方法,对390MPa级超低碳BH钢板热轧、冷轧、退火过程织构演变规律进行研究,并对不同冷轧月下量和不同退火工艺织构进行分析。结果表明:经冷轧变形后的钢板有较强的择优取向,具有典型的{112}〈110〉和{111}〈110〉织构,形变织构中的不利织构{001}〈110〉较强;冷轧压下率为80%时再结晶退火后钢板具有较强的Y织构,{111}〈112:织构取向密度高达11.7;退火温度和保温时间对a织构影响不大,提高退火温度和延长保温时间使y织构增强,r值增加。

Texture evolution in a 390 MPa grade high strength ultra low carbon bake hardening( ULCBH )steel in the process of hot rolling, cold rolling and annealing is studied by utilizing ODF texture analysis method. The effect of cold rolling reduction and annealing parameters on texture is measured. The results show that the ULC-BH sheet steel after cold rolling has a highly preferred orientation with typical /112/ 〈 110 〉 and /lll/ 〈 110 〉 texture, and strong unfavorable deformation texture /001 / 〈 110 〉. The increase of cold rolling reduction influeneed the strength ratio of favorable components to unfavorable components in the annealing textures. After annealing, a very strong y texture was obtained when cold rolling reduction reached 80% , which intensity peak was at 1111 / 〈 112 〉 component with f(g) value of 11.7. The annealing temperature and time had little influence on a texture, while increasing annealing temperature and extending holding time enhanced y texture intensity and r value.

参考文献

[1] De A.K.;Blauwe K.D. .Effect of dislocation density on the low temperature aging behavior of an ultra low carbon bake hardening steel[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(1/2):405-410.
[2] 朱士凤,宋起峰.CA1092车身轻量化的研究[J].汽车工艺与材料,2002(08):58-62.
[3] E. Kozeschnik .A contribution to the increase in yield strength during the bake hardening process[J].Steel Research,1997(5):224-230.
[4] Koen Lips;Xiaohong Yang;Koen Mols .The effect of coiling temperature and continuous annealing on the properties of bake hardenable IF steels[J].Steel Research,1996(9):357-363.
[5] 张倩;何崇智 .超深冲无间隙原子钢的织构与成形性[J].钢铁研究学报,1996,8(z1):15-19.
[6] Pero-Sanz J;Ruiz-Delgado M;Martinez V et al.Annealing texture for drawability:influence of the degree of cold rolling reduction for low-carbon andextra low-carbon ferritic steels[J].Materials Characterization,1999,43(05):303-309.
[7] P. Ghosh;B. Bhattacharya;R.K. Ray .Comparative study of precipitation behavior and texture formation in cold rolled-batch annealed and cold rolled-continuous annealed interstitial free high strength steels[J].Scripta materialia,2007(8):657-660.
[8] 熊道礼,毛卫民.含磷高强IF钢中FeTiP相的脱溶及硬化现象[J].北京科技大学学报,2000(04):350-353.
[9] Hirosuke INAGAKI .Fundamental aspect of texture formation in low carbon steel[J].ISIJ International,1994,34(04):313-321.
[10] Park YB;Lee DN;Gottstein G .Evolution of recrystallisation textures from cold rolling textures in interstitial free steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(4):289-298.
[11] 马全仓,毛卫民,杜磊,王利.不同织构组分对IF钢板R(θ)值起伏的影响[J].钢铁,2005(05):58-61.
[12] 杨平,李志超,毛卫民,赵子苏.钢中{111}〈112〉再结晶织构的形成[J].材料热处理学报,2009(03):46-52.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%