以L-丙交酯、乙交酯和ε-己内酯为原料开环聚合合成三元共聚物PLLGC.通过正交试验设计研究了预热温度、模压压力、模压温度、模压时间等因素对PLLGC模压材料性能的影响,确定了PLLGC材料最佳的模压工艺.研究了不同因素对PLLGC模压材料的拉伸强度、密度、模压后分子量及分子量分布的影响,通过极差分析结果表明,PLLGC三元共聚物的最佳模压工艺条件:预热温度为150℃,模压压力为8MPa,模压温度为100℃,模压时间为10min.
参考文献
| [1] | 王勤,王传栋,刘阳,马丽霞.L-丙交酯／ε-己内酯配比对共聚物微结构和性能的影响[J].高分子材料科学与工程,2012(06):61-64. |
| [2] | Simoes CL;Viana JC;Cunha AM .Mechanical Properties of Poly(epsilon-caprolactone) and Poly(lactic acid) Blends[J].Journal of Applied Polymer Science,2009(1):345-352. |
| [3] | Piotr Dobrzynski;Suming Li;Janusz Kasperczyk .Structure-Property Relationships of Copolymers Obtained by Ring-Opening Polymerization of Glycolide and epsilon-Caprolactone.Part 1.Synthesis and Characterization[J].Biomacromolecules,2005(1):483-488. |
| [4] | Ren T;Ren J;Jia X;Pan K .The bone formation in vitro and mandibular defect repair using PLGA porous scaffolds.[J].Journal of biomedical materials research, Part A,2005(4):562-569. |
| [5] | Hu YF;He Y;Wei J;Fan ZY;Dobrzynski P;Kasperczyk J;Bero M;Li SM .Hydrolytic degradation of glycolide/L-lactide/epsilon-caprolactone terpolymers initiated by zirconium(IV) acetylacetonate[J].Journal of Applied Polymer Science,2007(4):2451-2456. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%