采用超重力场自蔓延离心熔铸技术在TiB2基体中引入不同质量分数的(Ti,w)C成功制得大体积复相陶瓷.陶瓷主要由片状TiB2晶、球状TiC晶及不规则(Ti,w)C晶粒组成.随着WO3+Al反应物料含量的提高,体系绝热燃烧温度首先保持不变,随后呈明显增加趋势;并且高温下液相停留时间的延长、产物Stock对流的加快导致产物陶瓷中夹杂减少、(Ti,w)C相含量增加.各相晶粒的均匀化、(Ti,w)C相含量的提高将陶瓷硬度由15.89 GPa提升至23.4 GPa.
参考文献
| [1] | 黄雪刚;赵忠民;张龙;潘传增;苏官灵;曲振生;杨权;袁东.超重力下燃烧合成TiB2-（Ti,W）C共晶复合陶瓷结构[J].特种铸造及有色合金,2010(7):664-667. |
| [2] | Y.F.Yang;Q.C. Jiang.Reaction behaviour, microstructure and mechanical properties of TiC-TiB_2/Ni composite fabricated by pressure assisted self-propagating high-temperature synthesis in air and vacuum[J].Materials & design,2013Aug.(Aug.):123-129. |
| [3] | Cheloui, H.;Zhang, Z.;Shen, X.;Wang, F.;Lee, S..Microstructure and mechanical properties of TiB-TiB_2 ceramic matrix composites fabricated by spark plasma sintering[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201110/11(10/11):3849-3853. |
| [4] | Jinpeng Song;Chuanzhen Huang;Bin Zou;Hanlian Liu;Jun Wang.Microstructure and mechanical properties of TiB_2-TiC-WC composite ceramic tool materials[J].Materials & design,2012Apr.(Apr.):69-74. |
| [5] | 熊焰;傅正义.二硼化钛基金属陶瓷研究进展[J].硅酸盐通报,2005(1):60-64. |
| [6] | 高晓菊;满鹏;汪海东;白荣;李国斌;张涛.碳化钨硬质合金制备技术研究进展[J].硅酸盐通报,2013(1):71-76. |
| [7] | 杨统春 .TiB2-(W,Ti)C复合陶瓷刀具材料的研制及切削性能研究[D].山东大学,2013. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%