以乙酸锰和草酸为原料制备了草酸锰前驱体，并在氩气保护下将其焙烧得到了具有超电容特性的氧化亚锰，并对草酸锰前驱体的TGDSC曲线和XRD谱以及氧化亚锰的SEM形貌、EDS结果和电化学性能进行了分析。结果表明：在氩气气氛中焙烧草酸锰前驱体能够生成面心立方结构的氧化亚锰；500℃焙烧可得到粒径为0．5～2．0μm的小颗粒状氧化亚锰，其电容特性分布在0～-0．8V电位范围内，在1mol·L^-1 Li2SO4溶液中、0．1μg叫电流密度下其比容量约为49．7F·g^-1，经200次循环充放电后比容量衰减率仅为1．1％，适合用作超级电容器的负极材料。
Taking manganese acetate and oxalate as raw materials to prepare manganese oxalate precursor, and the precursor was roasted at argon atmosphere to obtain manganous oxide with supercapacitive characteristics. The TG-DSC curves and XRD patterns of manganese oxalate precursor, and the SEM morphology, EDS results and electrochemical performance were analyzed. The results show that manganous oxide with face-centered cubic structure was obtained by roasting manganese oxalate precursor at argon atmosphere. The small granular manganous oxide with diameter 0. 5- 2. 0 μm was got after roasting at 500 ℃, its capacitive characteristics distrihuted in the range of 0--0.8 V. The specific capacity was about 49.7 F·g^-1 under the condition of 1 mol ·L^-1 Li2SO4 solution and 0. 1 A ·g^-1 current density, and the lost rate of specific capacitance was only 1.1% after 200 charge-discharge cycles, so it could be used as anode material of supercapacitor.
参考文献
| [1] | 巢亚军,原鲜霞,马紫峰.复合材料在超级电容器中的应用研究进展[J].稀有金属材料与工程,2007(06):1110-1114. |
| [2] | Ataherian, F.;Wu, N.-L. .1.2 Volt manganese oxide symmetric supercapacitor[J].Electrochemistry communications,2011(11):1264-1267. |
| [3] | 贾志刚,岳林海,郑遗凡,徐铸德.有机-水溶剂体系中草酸锰结晶行为及其热分解特性的研究[J].无机化学学报,2007(01):181-188. |
| [4] | 宋志华,郭亨群,张春华,王国立,吴冲浒,吴其山,吴志军.纳米钨粉体的表征及其晶格畸变分析[J].材料导报,2009(10):106-108,111. |
| [5] | Li-Jie Sun;Xiao-Xia Liu;Kim King-Tong Lau;Liang Chen;Wei-Min Gu .Electrodeposited hybrid films of polyaniline and manganese oxide in nanofibrous structures for electrochemical supercapacitor[J].Electrochimica Acta,2008(7):3036-3042. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%