NiPnano Al2O3 composite coatings were deposited by electroless plating, and their microstructures were observed by SEM (scanning electron microscope). The microhardness and the wear resistance of the NiPnano Al2O3 composite coatings were measured using microhardness tester and blockonring tribometer, respectively, and the comparison with those of NiP coatings or NiPmicro Al2O3 coating was given. The influences of aging temperature on their hardness and wear resistance were analyzed. The results showed that the nano Al2O3 particles were distributed uniformly in the NiPAl2O3 coatings. Among three kinds of NiP based coatings, the hardness and wear resistance of NiPnano Al2O3 coatings were largest, and the maximum values could be obtained at 400 ℃. This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the NiP coatings.