以异丙醇铝为原料,采用溶胶凝胶法和浸渍提拉技术在玻璃载片上进行涂膜并考察了溶剂中乙醇含量对Al2 O3膜结构及性能的影响.结果表明:在总溶剂含量为66.4 mL时,水与无水乙醇的体积比为7∶1,经过8h回流后可得到稳定性良好的溶胶,溶胶的粘度为6.45 mPa·s；Al2O3薄膜的热稳定较好；所采用的烧结制度是0～100℃,升温速率为0.25℃/min,保温120 min；100～170℃,升温速率为0.5℃/min,保温120 min；170 ～400℃,升温速率为0.5℃/min,保温120 min；400～800℃,升温速率为1℃/min,保温120 min；最后自然冷却至室温即可得到性能良好的薄膜；膜表面光滑平整,薄膜平均孔径约为20.6449nm.
参考文献
| [1] | Malina R;Monica P;Jose M et al.Preparation and characterizeation of alumina supported silicalite membranes by sol-gel hydrothermal method[J].Journal of Membrane Science,2002,210:197-207. |
| [2] | Kikkinides E S;Stoitsas K A;Zaspalis V T .Correlation of structural and permeateon propertyes in sol-gel made nanoporous membranes[J].Journal of Colloid and Interface Science,2003,259:322-330. |
| [3] | Hao Y X;Li J S;Yang X J et al.Preparation of ZrO2-Al2 O3 composite membranes by sol-gel processs and their charactetizeation[J].Materials Science and Engngineering A,2004,367:243-247. |
| [4] | Ahmad AL;Idrus NF;Othman MR .Preparation of perovskite alumina ceramic membrane using sol-gel method[J].Journal of Membrane Science,2005(1/2):129-137. |
| [5] | 黄剑锋.溶腔-凝胶原理与技术[M].北京:化学工业出版社,2005 |
| [6] | 孙彩兰,张建中.溶胶凝胶法氧化铝分离膜制备工艺探讨[J].中国陶瓷工业,2007(05):11-14. |
| [7] | 章德玉,刘有智,谢五喜.PVA修饰的溶胶-凝胶法制备γ-Al2O3超滤膜的研究[J].膜科学与技术,2007(02):34-38. |
| [8] | 夏长荣;唐晔;杨萍华 等.PVA修饰的溶胶-凝胶法制备γ-氧化铝无机超滤膜[J].材料研究学报,1999,13(03):279-283. |
| [9] | 唐洪波,杨微,马冰洁.纳米TiO2的复合改性及其光催化性能[J].硅酸盐通报,2011(01):29-33. |
| [10] | 向洪平,沈汝梁,邓浩强,戴如勇,吕俊佳,葛建芳.TiO2溶胶稳定化制备工艺及机理研究[J].硅酸盐通报,2011(01):83-88. |
| [11] | 徐南平;邢卫红;赵宜江.无机膜分离技术与应用[M].北京:化学工业出版社,2003 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%