应用Fe/Mo/Al2O3载体载入式催化剂,以CO为碳源,分别通过火焰热解法和电加热热解法合成了碳纳米管.为了探究导致两种方法合成产物异同的原因,分别对两种方法中对应的实验操作和参数进行了对比分析.分析表明:(1)由于热解形式不同-火焰热解形式的剧烈性和电加热热解形式的缓和性,导致两种方法热解区气流扰动强度存在巨大差别,极大影响了产物的产量和质量；(2)由于合成温度不同,火焰热解法合成温度为830℃,可以合成单壁碳纳米管,而电加热热解法合成温度为790℃,仅能合成双壁、三壁碳纳米管.
参考文献
| [1] | Iijima S .Helical Microtubes of Graphite Carbon[J].Nature,1991,354:56-58. |
| [2] | Iijima S;Ajayan P M;IchihashiT .Growth Model for Carbon Nanotubes[J].Physical Review Letters,1992,69(21):3100-3103. |
| [3] | Guo T.;Thess A.;Colbert DT.;Smalley RE.;Nikolaev P. .CATALYTIC GROWTH OF SINGLE-WALLED NANOTUBES BY LASER VAPORIZATION[J].Chemical Physics Letters,1995(1/2):49-54. |
| [4] | Emmanuel Lamouroux;Philippe Serp;Yolande Kihn;Philippe Kalck .Identification of key parameters for the selective growth of single or double wall carbon nanotubes on FeMo/Al2O3 CVD catalysts[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2007(0):162-173. |
| [5] | M.J. Height;J.B. Howard;J.W. Tester .Flame synthesis of single-walled carbon nanotubes[J].Carbon,2004(11):2295-2307. |
| [6] | 孙保民,贾斌,郭永红,丁兆勇.Fe/Mo/Al2O3催化剂热解火焰法合成小直径少壁碳纳米管：催化剂焙烧与还原温度的影响[J].人工晶体学报,2011(02):459-464. |
| [7] | 郭永红,贾斌,孙保民,丁兆勇.Fe/Mo/Al2O3催化剂热解火焰法合成单壁、双壁和三壁碳纳米管：合成温度、取样时间与CO流量的影响[J].人工晶体学报,2011(04):947-952. |
| [8] | Randall L;Vander Wall;Lee J.Hall .Ferrocene as a Precursor Reagent for Metal-Catalyzed Carbon Nanoltubes:Competing Effects[J].Combustion and Flame,2002,130:27-36. |
| [9] | 王玉芳;蓝国祥 .碳纳米管的结构、对称性及晶格动力学[J].光散射学报,1999,11(01):36-45. |
| [10] | Dresselhaus M S;Eklund P C .Phonons in Carbon Nanotubes[J].Advances in Physics,2000,49(06):705-814. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%