作为钢铁炉外精炼及有色金属冶炼等冶金炉用内衬材料,镁铬砖在生产和使用过程中易产生有害的含Cr6+化合物,因此必须采取一定的措施防治"铬污染".在使用过程中,熔渣与材料组分反应引起的化学侵蚀,以及温度急剧变化引起的裂纹和结构剥落是导致RH炉用镁铬砖损毁的主要原因;熔渣与材料组分反应引起的化学熔蚀,熔体渗透引起的裂纹和结构剥落及炉内SO2气体引起的结构疏松是导致炼铜炉用镁铬砖损毁的主要原因.
As metallurgical furnace lining materials for secondary refining and nonferrous metal smelting, it is necessary to treat the pollution because Cr6+ compounds are formed when magnesia-chrome bricks are produced and used. The erosion caused by molten slag and the crack caused by temperature diversification are the main destroying mechanism of magnesia-chrome bricks used in RH furnaces while the corrosion caused by molten slag and the crack caused by melts penetration, the structure osteoporosis caused by SO2 are the main destroying mechanism of magnesiachrome bricks used in copper production furnaces.
参考文献
| [1] | Wilhelmi K A .System Cr2O3-CrO3[J].Acta Chemica Scandinavica,1968,22(08):2565. |
| [2] | Kaiser A;Sommer B;Woermann E .System CaO-Cr2O3-CrO3[J].Journal of the American Ceramic Society,1992,75(06):1463. |
| [3] | Panek Z .System CaO-Cr2O3[J].SILIKATY,1981,25(02):169. |
| [4] | Tanaka N;Takeychi A;Tanaka K .Mental recovery from the waste magnesia-chromia brick with are plasmas[J].J Energy Res Techn,2001,123(03):76. |
| [5] | 徐曾启.炉外精炼[M].北京:冶金工业出版社,2002:3. |
| [6] | Greskovich C;Stubican V S .System MgO-Cr2 O3-Al2O3[J].Journal of the American Ceramic Society,1968,51(01):42. |
| [7] | 王健东,潘波,杨晓峰.RH炉用高级镁铬砖的研究与侵蚀机理分析[J].炼钢,2007(04):43-46. |
| [8] | Alper A;McNally M R;Doman R C .System MgO-MgCr2O4[J].Journal of the American Ceramic Society,1964,47(01):30. |
| [9] | 王维邦.耐火材料工艺学[M].北京:冶金工业出版社,1994:5. |
| [10] | Hona Ming-hsiung;Hsua Chia-chan .Corrosion of magnesia-chrime in molten MgO-Al2O3-SiO2-CaO-FetO slag[J].Materials Chemistry and Physics,2008,110:247. |
| [11] | 彭容秋.重金属冶炼学[M].长沙:中南工业大学出版社,1991:9. |
| [12] | Liow J L;Tsinkis P;Gray P .Study of refracory wear in the tuyere region of a piece-smith nicki convertor[J].Canadian Metallurgical Quarterly,1998,2(37):99. |
| [13] | Petkov V;Jones P T;Boydens E .Chemical corrosion mechanisms of magnesia-chromite and chrome-free refractory bricks by copper metal and anode slag[J].Journal of the European Ceramic Society,2007,27:2433. |
| [14] | Barthel H .Wear of chromium-magnesite brick in copper smelting furnaces[J].Interceramics,1981,30:250. |
| [15] | 于仁红 .铜转炉介质对镁铬耐火材料侵蚀机理的研究[D].西安建筑科技大学,2002. |
| [16] | Bunting E N .System Cr2O3-SiO2[J].Journal of Research of the National Bureau of Standards,1931,6(06):947. |
| [17] | Deng Youngyue;Wang Houzhi .Influence of chrome-bearing sols vacuum impergnaton on the properties of magnesiachorme refractoy[J].CERAMICS INTERNATIONAL,2008,34:573. |
| [18] | Tsuchinari A;Okamoto H;Yokoyama Y.Chrome-free refractory for vacuum degassers[A].,1995:333. |
| [19] | Crites M.D.;Karakus M. .Interaction of chrome-free refractories with copper smelting and converting slags[J].Canadian Metallurgical Quarterly,2000(2):129-134. |
| [20] | Jones P E;Vleugels J;Volders I .A study of slag-infiltrated magnesia-chromite refractories using hybrid microwave heating[J].Journal of the European Ceramic Society,2002,22:903. |
| [21] | Crites M D;Schlesinger M E.Corrosion testing of chromefree refractories for copper production furnaces[A].,1999:187. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%