以工业TiOSO4液为原料,控制溶液pH值使TiOSO4液在复合模板剂十二胺和CTAB自组装超分子诱导作用下水解、缩聚和组装,制备出介孔TiO2前驱体.根据TG-DTG和DSC热分析结果确定对前驱体采用两步热处理方案.产物采用XRD、粒度分布、SEM及等温N2吸附进行分析表征.研究表明:在实验温度范围内,前驱体经热处理脱模后均得到锐钛型介孔TiO2,热处理温度的提高和时间的增长使产物结晶度增高,晶粒长大,但其介孔孔道逐渐收缩并坍塌破坏.采用350℃热处理1 h,500℃热处理1 h的热处理方案所得介孔TiO2的晶型与锐钛型TiO2标准物的最接近,晶粒尺寸L101=19.90 nm;粉末呈类球形,平均粒径为0.552μm;其介孔孔道分布窄,平均孔径为3.86 nm,BET比表面积为156.51 m2/g,孔容0.35 cm3/g.

参考文献

[1] Kresge C T;Leonowicz M E;Roth W J et al.[J].Nature,1992,359(6397):710.
[2] Beck J S;Vartuli J C;Roth W J et al.[J].Journal of the American Chemical Society,1992,114(27):10834.
[3] Mark E Davis .[J].Nature,2002,417(6891):813.
[4] 赵丽,余家国,赵修建,程蓓,张谢群,郭瑞.介孔纳米结构材料的研究与发展[J].稀有金属材料与工程,2004(01):5-10.
[5] Antonelli D M;Ying J Y .[J].Angewandte Chemie International Edition,1995,34(18):2014.
[6] Cabrera S.;Haskouri J.E. .Enhanced surface area in thermally stable pure mesoporous TiO_2[J].Solid state sciences,2000(5):513-518.
[7] Hui-suk Yun;Kuni'chi Miyazawa;Itaru Honma;Haoshen Zhou;Makoto Kuwabara .Synthesis of semicrystallized mesoporous TiO_2 thin films using triblock copolymer templates[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2003(4):487-494.
[8] Cassiers Cristof;Linssen Thierry;Mathieu Mariska et al.[J].Journal of Physical Chemistry B,2004,108(12):3713.
[9] Ruiqin Tan;Yu He;Yongfa Zhu et al.[J].Journal of Materials Science,2003,38(19):3973.
[10] Antonelli D M .[J].Microporous and Mesoporous Materials,1999,30(2-3):315.
[11] Evi Beyers;Pegie Cool;Etienne F Vansant .[J].Journal of Physical Chemistry B,2005,109(20):10081.
[12] He J.;Yang XB.;Evans DG.;Duan X. .New methods to remove organic templates from porous materials[J].Materials Chemistry and Physics,2003(1):270-275.
[13] Zhang Z B;Wang C C;R Zakaria R et al.[J].Journal of Physical Chemistry B,1998,102(52):10871.
[14] Devi G Sarala;Takeo Hyodo;Yasuhiro Shimizu et al.[J].Sensors and Actuators B-Chemical,2002,87(01):122.
[15] Pizzio Luis René .[J].Materials Letters,2005,59(8-9):994.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%