采用DSC、XRD 检测方法,分析了经673 K((Tg-100 K)＜T＜Tg)不同时间(20,40,60 min)预退火处理后,Fe68Ni1Al5GazP9.65B4.6Si3C6.75非晶合金的玻璃转变温度Tg、起始晶化温度Tx、晶化峰温度Tp、玻璃转变过程中的比热容增量△Cp,g的变化以及经823 K晶化反应后的XRD图谱.结果表明:Fe68Ni1Al5Ga2P9.65B4.6Si3C6.75非晶合金的玻璃转变温度Tg和比热容增量△Cp,g随预退火时间的延长而逐步增加；起始晶化温度Tx和第一晶化峰温度Tp1随预退火时间呈现出逐渐减小的趋势；其晶化后样品衍射峰形貌相似,衍射峰的强度略有不同.利用结构弛豫理论对实验结果进行了分析.
参考文献
| [1] | Chang YK.;Pong WF.;Tsai MH.;Chen YY.;Chiou JW.;Jan JC. Chien FZ.;Tseng PK.;Dann TE.;Leu MS.;Chin TS.;Cheng YH. .The effect of annealing time on the electronic structure of the Fe-Cu-Nb-Si-B alloys[J].Journal of Electron Spectroscopy and Related Phenomena,2001(0):831-835. |
| [2] | Kim KB;Warren PJ;Cantor B .Structural relaxation and glass transition behavior of novel (Ti33Zr33Hf33)(50)(Ni50Cu50)(40)Al-10 alloy developed by equiatomic substitution[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2007(32/40):3338-3341. |
| [3] | Zhang G P;Liu Y;Zhang B .[J].Scripta Materialia,2006,54(05):897. |
| [4] | Tanga J C;Zhou L;Tan D Q et al.[J].Journal of Alloys and Compounds,2005,394(1-2):215. |
| [5] | 王敬丰,柳林,邹辉,蒲健,肖建中.大块金属玻璃Pd40Ni10Cu30P20结构弛豫的研究[J].稀有金属材料与工程,2005(01):98-101. |
| [6] | Chen H S;Inoue A;Masumoto T .[J].Journal of Materials Science,1985,20:2417. |
| [7] | Cohen M H;Grest G S .[J].Physical Review B,1979,20(03):1077. |
| [8] | G-rest G S;Cohen M H .[J].Physical Review B,1980,21(09):4113. |
| [9] | 胡勇,寇生中,丁雨田,许广济.预退火温度对Cu基块状非晶玻璃转变及晶化的影响[J].材料导报,2007(z1):439-441. |
| [10] | 梅金娜,李金山,寇宏超,邢力谦,傅恒志,周廉.Ti40Zr25Ni8Cu9Be18非晶合金的晶化行为研究[J].稀有金属材料与工程,2007(07):1215-1218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%