研究了63～292K热力学过冷度范围内,Cu-Ni单相合金的凝固组织演化规律,分析了负温度梯度熔体凝固过程中的形核与再辉行为.结果表明:①负温度梯度熔体凝固的冷却曲线上有较明显的形核特征;②在负温度梯度熔体凝固冷却曲线的快速再辉阶段,出现了明显的"二次再辉"特征,此"二次再辉"的本质有别于慢速凝固阶段的二次再辉,因此称之为"伪再辉".
参考文献
| [1] | 坚增运,严文.深过冷金属熔体中单晶形成的临界条件[J].自然科学进展,1999(02):165. |
| [2] | 宋广生,杨根仓,周尧和,张欣梅,沈军,李庆春.纳米晶Al88Ce2Ni10铝合金的形成[J].中国有色金属学报,1997(02):86-89. |
| [3] | XIE Faqin,LI Jinshan,FU Hengzhi.An investigation on supercooling directional solidification process of Cu-Ni single phase alloy[J].科学通报（英文版）,2000(02):131-134. |
| [4] | 李順朴;赵德乾;陈熙琛 .深过冷条件下Ni-Sn合金的伪共生区与形核特点[J].,1995,31(07):304. |
| [5] | Piccoae T J;Wu Y;Shiohara Y .[J].Metallurgical and Materials Transactions,1987,18:925. |
| [6] | Lipton J;Glicksman M E;Kurz W .[J].Materials Science and Engineering,1984,65:57. |
| [7] | Lipton J;Kurz W;Trivedi R .[J].Acta Materialia,1987,4:957. |
| [8] | Boettinger W J;Coriell S R;Trivedi R.[A].Claitor's Publishing Division,Baton Rouge,LA,1988:13. |
| [9] | 杨根仓;魏炳波;周尧和 .[J].材料科学与进展,1990,3:228. |
| [10] | Wilinecker R;Herlach D M;Feuerbacher B .[J].Materials Science and Engineering,1988,98:85. |
| [11] | Valencial J J;McCullough C;Levi G G et al.[J].Acta Materialia,1989,37:2517. |
| [12] | Bertero G A;Homeister W H;Robinson M B .[J].Metallurgical and Materials Transactions,1991,22:2723. |
| [13] | 李德林 .深过冷快淬Ni基合金与三维非晶的形成及性能研究[D].西安:西北工业大学,1990. |
| [14] | 谢发勤,李金山,傅恒志.负温度梯度熔体中晶体生长取向与控制[J].甘肃工业大学学报,2002(03):19-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%