对激光快速成形粉末高温合金的组织和性能进行了研究.结果表明,激光快速成形沉积态组织中γ'沉淀相的析出受到抑制,γ'沉淀相在γ基体中的体积分数小,γ'相的平均尺寸显著细化.在热处理制度为1165℃固溶2 h空冷+760℃时效16 h空冷的基础上,适当延长时效时间将有助于细小γ'沉淀相的长大,使固溶时效态组织的抗拉强度提高到P/M+HIP标准的89%,屈服强度已经接近粉末冶金水平,显示出较好的强化效果.
参考文献
| [1] | David Abbott;Frank Arcella.[J].Current Advances in Materials and Processes,1998(05):29. |
| [2] | Arcella F G;Froes F H .[J].Journal of Metals,2000,52(05):28. |
| [3] | Frank Arcella;Abbou D H;House M A.[A].Albuquerque:American Institute of Aeronautics and Astronautics Incorporation,2000 |
| [4] | Snow D B;Breinan E M;Kear B H.[A].Baton Rouge,LA:Alaitors Publishing Div,1980 |
| [5] | Gaumann, M., -;Cleton, F;Wagniere, JD;Kurz, W., -;Henry, S .Epitaxial laser metal forming: analysis of microstructure formation[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(1-2):232-241. |
| [6] | Gaumann M;Bezencon C;Canalis P et al.[J].Acta Materialia,2001,49:1051. |
| [7] | Hongqing Sun;Minlin Zhong;WeMin Liu et al.[J].Proceedings of Spie,2002,5629:84. |
| [8] | Minlin Zhong;Lin Yang;Wenjin Liu et al.[J].Proceedings of Spie,2002,5629:59. |
| [9] | Sexton L;Lavin S;Byrne G et al.[J].Journal of Materials Processing Technology,2002,122:63. |
| [10] | Blackwell P L .[J].Journal of Materials Processing Technology,2005,170(1-2):240. |
| [11] | 杨海欧,陈静,李延民,冯莉萍,林鑫,黄卫东.Rene95高温合金激光快速成形试样的力学性能[J].稀有金属材料与工程,2003(04):276-279. |
| [12] | 赵晓明,陈静,何飞,谭华,黄卫东.激光快速成形Rene88DT高温合金开裂机理研究[J].稀有金属材料与工程,2007(02):216-220. |
| [13] | 黄卫东 .国家高技术研究发展计划课题自验收报告[R].北京,2005. |
| [14] | 张永忠,石力开,章萍芝,席明哲,程晶,徐骏.激光快速成形镍基高温合金研究[J].航空材料学报,2002(01):22-25. |
| [15] | 马莉萍 .激光多层涂覆定向凝固的研究[D].西安:西北工业大学,2002. |
| [16] | 陈静,杨海欧,杨健,黄卫东.高温合金与钛合金的激光快速成形工艺研究[J].航空材料学报,2003(z1):100-103. |
| [17] | 赵晓明 .激光快速成形Rene′88DT高温合金力学性能研究[D].西北工业大学,2006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%