Alumina specimens were joined together with thin aluminium interlayer at 750 and 900°C under different applied pressures and holding time in air. Flexural strength of the joints was then measured using a standard four-point bend test method. Characterization of the interface was carried out to correlate the increase in flexural strength with the applied pressure, holding temperature and time. The study showed that the strength of joint is affected by all three parameters, i.e., processing temperature, holding time as well as applied pressure.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | D. Treheux, P. Lourdin, V. Guipont and D. Juve: J. Phys. III France, 1994, 4, 1883.[2 ] M.G. Nicholas: Joining of Ceramics: 1st edn, Chapman and Hall, 1990, 73.[3 ] E. Candan: Turkish J. Eng. Env. Sci, 2002, 26, 1.[4 ] A.H. Carim and C.H. Mohr: Mater. Lett., 1997, 33, 195.[5 ] A. Meier, P.R. Chidambaram and G.R. Edwards: Acta Mater., 1998, 12, 4453.[6 ] J.Y. Kim, J.S. Hardy and K.S. Weil: J. Am. Ceram. Soc., 2005, 9, 2521.[7 ] F. Barbier, C. Peytour and A. Revcolevschi: J. Am. Ceram. Soc., 1990, 6, 1582.[8 ] N. Shao, J.W. Dai, G.Y. Li, H. Nakae and T. Hane: Mater. Lett., 2004,58, 2041.[9 ] J.T. McKeown, J.D. Sugar, Joseph, R. Gronsky and A.M. Glaeser: Mater. Charact., 2006, 57, 50.[10] A.W. Hey: Joining of Ceramics, Ist ed., Chapman and Hall, 1990, 56.[11] O.M. Akselsen: J. Mater. Sci., 1992, 2, 1989.[12] K. Suganuma, Y. Miyamoto and M. Koizumi: Ann. Rev. Mater. Sci., 1988, 18, 47.[13] V.A. Greenhut and T.R. Chapman: J. Am. Ceram. Soc., 2003, 138, 61.[14] R.M.D. Nascimento, A.E. Martinelli and A.J.A. Buschinelli: Cer^amica, 2003, 49, 178.[15] J.Y. Kim and K.S. Weil: J. Am. Ceram. Soc., 2007, 12, 3830.[16] E.J. Pavlina, A.M. Meier, P. Monteleone and J.D. Weigner: J. Mater. Sci., 2007, 42, 705.[17] S.Y. Chang, T.H. Chaung and C.L. Yang: J. Electro. Mater., 2007, 9, 119.[18] A. Ibrahim and F. Hasan: Joining of Advanced and Specialty Material X: Proc. Mater. Sci. & |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%