采用示差扫描量热仪(DSC)测量了轧辊用新型高速钢材料不同类型碳化物的析出温度,并采用场发射扫描电镜(FESEM)观察其典型形貌和测定其相结构.在各特征温度下,分别对轧辊用新型高速钢保温15、20、25和30 min后快冷,采用金相统计软件对碳化物的体积分数进行了统计.结果表明:轧辊用高速钢在1300℃的温度快冷后,保温25 min时MC相的体积分数有最大值；1220 ℃快冷后MC和M2C相的体积分数均在保温20 min时有最大值；1150℃快冷后MC的体积分数一直增加,M2C的体积分数在保温20 min时有最大值,25 min时有最小值,而M6C的体积分数先增加后减少,保温20 min时有最大值.
参考文献
| [1] | 王强,杨涤心,魏世忠,龙锐,李炎.轧辊用高钒高速钢、高铬铸铁滚动磨损性能研究[J].材料热处理学报,2006(06):84-88. |
| [2] | C. S. Li;X. H. Liu;G. D. Wang;X. M. He .Three-dimensional FEM analysis of work roll temperature field in hot strip rolling[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2002(10):1147-1150. |
| [3] | 符寒光,汪长安.高速钢轧辊的热处理工艺[J].金属热处理,2010(09):60-65. |
| [4] | Rodenburg C;Rainforth W M .A quantitative analysis of the influence of carbides size distributions on wear behavior of high-speed steel in dry rolling/sliding contact[J].Acta Materialia,2007,55(07):2443-2454. |
| [5] | Hongshuang Di;Xiaoming Zhang;Guodong Wang .Spheroidizing kinetics of eutectic carbide In the twin roll-casting of M2 high-speed steel[J].Journal of Materials Processing Technology,2005(3):359-363. |
| [6] | 张彩东,蒋斌,杨琴,丁培道.M2高速钢工业铸带中共晶碳化物及其演化[J].材料热处理学报,2009(03):107-110. |
| [7] | Hwang K C;Lee S;Lee H C .Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls.Part Ⅰ:Microstructure analysis[J].Materials Science and Engineering A,1998,254(01):282-295. |
| [8] | Shizhong Wei;Jinhua Zhu;Liujie Xu .Effects of vanadium and carbon on microstructures and abrasive wear resistance of high speed steel[J].Tribology International,2006(7):641-648. |
| [9] | Wei S Z;Zhu J H;Xu L J et al.Effects of carbon on microstructures and properties of high vanadium high-speed steel[J].Materials & Design,2006,27(01):58-63. |
| [10] | Bochnowski W.;Leitner H.;Major L.;Ebner R.;Major B. .Primary and secondary carbides in high-speed steels after conventional heat treatment and laser modification[J].Materials Chemistry and Physics,2003(2/3):503-506. |
| [11] | M.A. de Carvalho;R.R. Xavier;C. da Silva Pontes Filho .Microstructure, Mechanical Properties and Wear Resistance of High Speed Steel Rolls for Hot Rolling Mills[J].Iron & Steelmaker,2002(1):27-32. |
| [12] | ZHOU Bin,SHEN Yu,CHEN Jun,CUI Zhen-shan.Breakdown Behavior of Eutectic Carbide in High Speed Steel During Hot Compression[J].钢铁研究学报（英文版）,2011(01):41-48. |
| [13] | Dennis W. Hetzner .Refining carbide size distributions in M1 high speed steel by processing and alloying[J].Materials Characterization,2001(2/3):175-182. |
| [14] | Qu, H.;Liao, B.;Liu, L.;Li, D.;Guo, J.;Ren, X.;Yang, Q..Precipitation rule of carbides in a new high speed steel for rollers[J].Calphad: Computer Coupling of Phase Diagrams and Thermochemistry,2012:144-150. |
| [15] | 邓玉昆;陈景榕;王世章.高速工具钢[M].北京:冶金工业出版社,2002:77-78,108-110. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%