采用高能等离子喷涂技术制备了Sm2Zr2O7热障涂层,用X射线衍射(XRD)、扫描电镜(SEM)等手段研究了涂层的相成分、微观组织;采用拉伸法和水淬法测试了涂层的结合强度及热冲击性能.结果表明,喷涂前后Sm2Zr2O7相成分未发生变化,表现出良好的相稳定性能.所制备的Sm2Zr2O7涂层结构致密,涂层各界面结合紧密.涂层的孔隙率仅为4.72%,结合强度为29MPa.涂层在经历20次热冲击后从表面层/金属粘结层界面处脱落,熔融颗粒内部纵向显微裂纹及熔融颗粒之间彼此分离所形成的横向裂纹的共同作用导致了涂层的失效.
参考文献
| [1] | Nitin P. Padture;Maurice Gell;Eric H. Jordan .Thermal Barrier Coatings for Gas-Turbine Engine Applications[J].Science,2002(5566):280-284. |
| [2] | Parks P k;Hoffman E E;Lee W Y et al.Thermal barrier coatings issues in advanced land-based gas turbines[J].Journal of Thermal Spray Technology,1997,6(02):187-192. |
| [3] | Miller R A .Thermal barrier coatings for aircraft engines:history and directions[J].Journal of Thermal Spray Technology,1997,5(01):35-42. |
| [4] | W. Beele;G. Marijnissen;A. van Lieshout .The evolution of thermal barrier coatings -- status and upcoming solutions for today's key issues[J].Surface & Coatings Technology,1999(0):61-67. |
| [5] | Cao X Q;Vasseh R;Stoever D .Ceramic materials for thermal barrier coatings[J].Journal of the European Ceramic Society,2000,24:1-10. |
| [6] | Qiang X;Wei P;Jingdong.W et al.Preparation and thermophysical proeprties of Dy2Zr2O7 ceramic for thermal barrier coatings[J].Materials Letters,2005,59:2804-2807. |
| [7] | Ken Kurosaki;Takanori Tanaka;Takuji Maekawa .Thermophysical properties of SrY_2O_4[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):304-308. |
| [8] | 张红松,李振军,徐强,王富耻,王全胜,刘玲.大气等离子喷涂Sm2Zr2O7热障涂层的微观组织[J].材料热处理学报,2008(03):163-167. |
| [9] | 姜超,丁洁,李爱国,武兵书,陈蕴博.Al2 O3与ZrO2复合粉涂层的组织形貌分析[J].金属热处理,2005(12):58-60. |
| [10] | 王振林;韩永;许晋生.金属热喷涂技术及其应用[M].北京:纺织工业出版社,1992:10-22. |
| [11] | Anand Kulkarni;A. Vaidya;A. Goland .Processing effects on porosity-property correlations in plasma sprayed yttria-stabilized zirconia coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):100-111. |
| [12] | Friis M.;Wigren J.;Persson C. .Influence of particle in-flight characteristics on the microstructure of atmospheric plasma sprayed yttria stabilized ZrO2[J].Surface & Coatings Technology,2001(2/3):115-127. |
| [13] | Tekmen C.;Ozdemir I.;Celik E. .Failure behaviour of functionally gradient materials under thermal cycling conditions[J].Surface & Coatings Technology,2003(0):1101-1105. |
| [14] | Guo HB;Vassen R;Stover D .Thermophysical properties and thermal cycling behavior of plasma sprayed thick thermal barrier coatings[J].Surface & Coatings Technology,2005(1):48-56. |
| [15] | Zhou B.;Kokini K. .Effect of pre-existing surface crack morphology on the interfacial thermal fracture of thermal barrier coatings: a numerical study[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):271-279. |
| [16] | Khor K A;Gu Y W .Effects of residual stress on the performance of plasma sprayed functionally graded ZrO2/NiCoCrAlY coatings[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2000,277:64-76. |
| [17] | 张红松,张政,陈晓鸽,刘建英.等离子喷涂Sm_2Zr_2O_7热障涂层残余热应力[J].中国陶瓷,2010(04):38-41. |
| [18] | 马壮,王全胜,王富耻,吕广庶.涂层基体条件对梯度涂层残余应力影响研究[J].材料工程,2002(04):15-18,37. |
| [19] | 张红松,王富耻,马壮,李淑华,冼文锋,成志芳.等离子喷涂ZrO2涂层的火焰喷烧和水淬热冲击[J].表面技术,2006(04):30-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%