研究了NiAl金属间化合物在拉伸条件下的超塑性变形行为和机理.结果表明:用常规精铸工艺和定向凝固工艺制备的NiAl及NiAl基合金都表现出典型的超塑性特征.根据这些合金的显微组织的特点可以分为3类:多相等轴晶组织(NiAl-9Mo,NiAl-25Cr,NiAl-20Fe-Y、Ce,NiAl-30Fe-Y);单相等轴晶组织(NiAl)和柱状晶组织(NiAl-27Fe-3Nb,NiAl-15Cr,NiAl-5Mo-0.5Hf).相应的超塑性变形机理分别是晶界滑动伴随着动态回复,动态回复和再结晶以及晶内的位错滑移.
参考文献
| [1] | Miracle D B .[J].ACTA METALLURGICA ET MATERIALIA,1993,41:649-703. |
| [2] | Sherby O D;Wadsworth J .[J].Progress in Materials Science,1989,33:169-209. |
| [3] | 陈荣石;郭建亭;殷为民 .[J].金属学报,1998,34:1121-1126. |
| [4] | ChenRS;Guo JT;Yin W M .[J].Scripta Materialia,1999,40:209-216. |
| [5] | 崔传勇,郭建亭,齐义辉,叶恒强.定向凝固NiAl-28Cr-5.8Mo-0.2Hf合金的高温拉伸蠕变行为[J].金属学报,2002(04):342-346. |
| [6] | Qi YH;Guo J T;CUI C Y et al.[J].Materials Letters,2002,57:552-557. |
| [7] | Zhou J;Guo J T;Submitted to Z.[J].Metallkd |
| [8] | Backofen W A;Turner I R;Avery D H .[J].Transactions of the ASME,1964,57:980-987. |
| [9] | Noebe R D;Cullers C L.[J].Journal of Materials Research,1992(07):604-612. |
| [10] | Du X H;Guo J T;Zhou B D .[J].Scripta Materialia,2001,45:69-75. |
| [11] | Lautenschlager E P;Tisone T C;Brittain J O .[J].Phas Stat Sol,1967,20:443-449. |
| [12] | Deng W;Xiong L Y;Lung C W et al.[J].Materials Science Forum,1995,175:339-343. |
| [13] | Schum R W;Badura-Gergen K;Kummerle E A .[J].Physical Review,1996,54:849-855. |
| [14] | Nieh T G;Wadsworth J .[J].International Materials Reviews,1999,44:59-78. |
| [15] | Fukuyo H;Tsai H C;yama T et al.[J].ISIJ International,1991,31(01):76-86. |
| [16] | Novikov I I;Portnoy V K;Titov A O et al.[J].Scripta Materialia,2000,42:899-905. |
| [17] | TakasugiT;KishinoJ;HanadaS .[J].ACTA METALLURGICA ET MATERIALIA,1993,41(04):1009-1019. |
| [18] | Kim W Y;Hanada S;Takasugi T .[J].Acta Materialia,1998,46:5701-5709. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%