为探索适于中温条件下使用的固体氧化物燃料电池的阴极材料,用甘氨酸-硝酸盐法(GNP法)制备了Gd0.8Sr0.2CoO3(GSC)阴极粉体,用X-ray衍射考察了GSC的成相温度.采用丝网印刷法将GSC沉积在(Sm2O3)0.2(CeO2)0.8(SDC)圆片上,制成对称阴极,在不同温度下烧结.用交流阻抗谱从500℃到750℃测量了GSC阴极和SDC电解质之间的界面电阻.结果表明,用甘氨酸-硝酸盐法制备的GSC粉体的成相温度比传统固相法降低了400℃～500℃;700℃时,GSC阴极的界面电阻仅为0.26 Ω·cm2.
参考文献
| [1] | Steele BCH.;Uchino S.;Hori KM. .Kinetic parameters influencing the performance of IT-SOFC composite electrodes[J].Solid state ionics,2000(1/4):445-450. |
| [2] | Murray EP.;Barnett SA. .(La,Sr) MnO3-(Ce,Gd)O2-x composite cathodes for solid oxide fuel cells[J].Solid state ionics,2001(3/4):265-273. |
| [3] | 程继贵,李海滨,刘杏芹,孟广耀.燃料电池Ni/SCO阳极流延膜的性能研究[J].稀有金属材料与工程,2003(12):986-990. |
| [4] | 万吉高,王开军,陈家林.低温处理制备无团聚氧化锆超细粉末的研究[J].稀有金属材料与工程,2000(05):347-349. |
| [5] | Phillipps M.B.;Yamamoto O.;Sammes N.M. .Gd_(1-x)A_xCo_(1-y)Mn_yO_3 (A = Sr, Ca) as a cathode for the SOFC[J].Solid state ionics,1999(1/4):131-138. |
| [6] | Boivin JC.;Mairesse G. .Recent material developments in fast oxide ion conductors [Review][J].Chemistry of Materials,1998(10):2870-2888. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%