用乙烯-醋酸乙烯酯共聚物(EVA)对尼龙6(PA6)进行增韧,加入乙烯-醋酸乙烯酯共聚物与马来酸酐的接枝物(EVA-g-MAH)进行原位反应增容,在反应型双螺杆挤出机上实现反应增容共混过程,制备出了具有超韧性的PA6/EVA/EVA-g-MAH三元共混合金.探讨了EVA-g-MAH对PA6/EVA的原位反应及增容机理,用高倍扫描电镜考察了合金材料的亚微相态.结果表明,EVA-g-MAH的加入使合金中EVA粒子的粒径减小数倍,合金的冲击强度大幅度提高.另外,还利用Molau实验验证了原位反应增容效果.
参考文献
| [1] | Olabisi O;Robeson L M;Shaw M T.Polymer-Polymer Miscibility[M].New York:Academic Press,1979 |
| [2] | Majumar B;Keskkula H;Paul D R .[J].Polymer,1993,35:1386. |
| [3] | Oshiski A J;Keskkula H;Paul D R .[J].POLYMER,1992,33:286. |
| [4] | Sathe S N;Srinivasa G S .[J].Journal of Applied Polymer Science,1994,53:239. |
| [5] | 宋国君,舒文艺.提高聚合物共混相容性的反应性聚合物[J].功能高分子学报,1996(01):137-147. |
| [6] | Dijkstra K;Laoe J;Gaymans R J .[J].Polymer,1995,35:315. |
| [7] | Borggreve R J M;Gaymans R J .[J].Polymer,1989,30:78. |
| [8] | Borggreve R J M;Gaymans R J .[J].Polymer,1989,30:71. |
| [9] | Epstein B N .[P].U S Patent:4174358,1979. |
| [10] | Majumdar B;Keakkula H;Paul D R .[J].Polymer,1994,35:1386. |
| [11] | Oshinski A J;Keakkula H;Paul D R .[J].POLYMER,1992,33:268. |
| [12] | Gilmore D W;Modic M J.[J].Plastics Engineering,1989:29. |
| [13] | Molau G E.[J].Journal of Polymer Science,1965:4235. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%